InnoPlus HD1100J HDPE
InnoPlus HD1200J HDPE
InnoPlus HD1600J HDPE
InnoPlus HD1600JP HDPE
InnoPlus HD2200JP HDPE
InnoPlus HD2208J HDPE
InnoPlus HD2209J HDPE
InnoPlus HD2308J HDPE
InnoPlus HD3000C HDPE
InnoPlus HD3001C HDPE
InnoPlus HD3200B HDPE
InnoPlus HD3502C HDPE
InnoPlus HD4200B HDPE
InnoPlus HD5000S HDPE
InnoPlus HD5200B HDPE
InnoPlus HD6000C HDPE
InnoPlus HD6000F HDPE
InnoPlus HD6001C HDPE
InnoPlus HD6200B HDPE
InnoPlus HD6366M HDPE
InnoPlus HD6366MB HDPE
InnoPlus HD6376EB HDPE
InnoPlus HD6396EB HDPE
InnoPlus HD6600B HDPE
InnoPlus HD6800B HDPE
InnoPlus HD7000F HDPE
InnoPlus HD7000H HDPE
InnoPlus HD7200B HDPE
InnoPlus HD8000F HDPE
InnoPlus HD8100M HDPE
InnoPlus HD8100MB HDPE
InnoPlus HD8200B HDPE
InnoPlus HD1100J
高密度聚乙烯
PTT Global Chemical Public Company Limited
产品说明：
InnoPlus HD1100J and HD1600J are high density polyethylene injection molding grade. They are tailored with narrow molecular weight distribution (MWD) and high flow ability. They have optimum strength property which used for general part, auto part, toy and house ware.
Typical Application: Toys, Auto parts, Household products
Typical Application: Toys, Auto parts, Household products
InnoPlus HD1100J 物性表
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| RoHS 合规性 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.958 | g/cm3 | ASTM D1505 |
| 熔流率（熔体流动速率）(190°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| ESCR - condition B, 25% Igepal, F50 | Initial Break | ASTM D1693 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度(邵氏 D) | 64 | ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | ASTM D638 | ||
| 屈服 | 29.4 | MPa | ASTM D638 |
| 断裂 | 22.6 | MPa | ASTM D638 |
| 伸长率(断裂) | 60 | % | ASTM D638 |
| 明显的弯曲模量 | 981 | MPa | ASTM D747 |
| 弯曲模量 | 1230 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度1 | 39 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | 116 | °C | ASTM D15252 |
| 熔融峰值温度 | 128 | °C | ASTM D3418 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 料筒后部温度 | 165 到 190 | °C | |
| 料筒中部温度 | 165 到 190 | °C | |
| 料筒前部温度 | 165 到 190 | °C | |
| 射嘴温度 | 180 到 195 | °C |
| 备注 | |
|---|---|
| 1 . | Complete break |
| 2 . | 速率 A (50°C/h), 压 力1 (10N) |