VESTAMID? E E55-S3
聚酰胺12
Evonik Industries AG
产品说明：
Typical Applications: alpine ski boots, sports shoe soles, pneumatic lines, rolls, technical films
PA 12 elastomers, the most important subgroup of polyamide elastomers, belong to the increasingly important material class of thermoplastic elastomers (TPE). Because of their excellent properties, they are indispensable in many applications.
PA 12 elastomers, the most important subgroup of polyamide elastomers, belong to the increasingly important material class of thermoplastic elastomers (TPE). Because of their excellent properties, they are indispensable in many applications.
PA 12 elastomers are block copolymers consisting of PA 12 segments and polyether segments. PA 12-rich products have the major properties of PA 12, while the elastomer characteristics become more apparent with increasing polyether content. That is the polymers become more flexible, with higher impact strength at cold temperatures.
现货PA12 E55-S3 (高弹性 消声齿轮专用 ) PA12 E55-S3货源稳定
VESTAMID? E E55-S3 物性表
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.03 | g/cm3 | ISO 1183 |
| 收缩率1 | ISO 294-4 | ||
| 垂直流动方向 | 0.90 到 1.5 | % | ISO 294-4 |
| 流动方向 | 0.60 到 1.1 | % | ISO 294-4 |
| 吸水率(饱和, 23°C) | 1.1 | % | ISO 62 |
| 粘数 | 190 | cm3/g | ISO 307 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度(邵氏 D) | 55 | ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 220 | MPa | ISO 527-2 |
| 拉伸应力 | ISO 527-2 | ||
| -- | 38.0 | MPa | ISO 527-2 |
| 50% 应变 | 17.0 | MPa | ISO 527-2 |
| 拉伸应变(断裂) | 200 | % | ISO 527-2 |
| 拉伸蠕变模量(1000 hr) | 100 | MPa | ISO 899-1 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179/1eA | ||
| -30°C, 完全断裂 | 22 | kJ/m2 | ISO 179/1eA |
| 23°C | 无断裂 | ISO 179/1eA | |
| 简支梁无缺口冲击强度 | ISO 179/1eU | ||
| -30°C | 无断裂 | ISO 179/1eU | |
| 23°C | 无断裂 | ISO 179/1eU |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 热变形温度 | |||
| 0.45 MPa, 未退火 | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, 未退火 | 45.0 | °C | ISO 75-2/A |
| 维卡软化温度 | |||
| -- | 160 | °C | ISO 306/A |
| -- | 100 | °C | ISO 306/B |
| 线形热膨胀系数 | ISO 11359-2 | ||
| 流动 : 23 到 55°C | 2.0E-4 | cm/cm/°C | ISO 11359-2 |
| 横向 : 23 到 55°C | 2.0E-4 | cm/cm/°C | ISO 11359-2 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 表面电阻率 | 1.0E+13 | ohms | IEC 60093 |
| 体积电阻率 | 1.0E+11 | ohms·cm | IEC 60093 |
| 介电强度 | 38 | kV/mm | IEC 60243-1 |
| 相对电容率 | IEC 60250 | ||
| 23°C, 100 Hz | 9.50 | IEC 60250 | |
| 23°C, 1 MHz | 4.30 | IEC 60250 | |
| 耗散因数 | IEC 60250 | ||
| 23°C, 100 Hz | 0.095 | IEC 60250 | |
| 23°C, 1 MHz | 0.11 | IEC 60250 | |
| 漏电起痕指数(解决方案 A) | 600 | V | IEC 60112 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UL 阻燃等级(1.60 mm) | HB | UL 94 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 建议的最大水分含量 | 0.10 | % | |
| 加工（熔体）温度 | 190 到 230 | °C | |
| 模具温度 | 20.0 到 40.0 | °C |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 建议的最大水分含量 | 0.10 | % | |
| 熔体温度 | 190 到 230 | °C |
| 备注 | |
|---|---|
| 1 . | determined on 3mm sheets with film gate at rim, mold temp. 80°C |