上海汇堡材料科技有限公司
Ixef FC-1022
聚丙烯酰胺
50% 玻璃纤维增强材料
Solvay Specialty Polymers
产品说明：
Ixef? FC-1022 is a 50% glass-fiber reinforced, general purpose polyarylamide compound that exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance. Ixef? FC-1022 is approved for food contact and meets FDA regulations for Ixef? FC-1022 NT 000 (natural) and Ixef? FC-1022 BK 000 (black) based on clearances granted by FCN 001242 for repeated use food contact applications with all food types, under FDA conditions of use B through H as described in Tables 1 and 2 of 21 CFR 176.170(c).
Ixef? FC-1022 物性表
| 基本信息 | |
|---|---|
| 黄卡编号 | |
| 填料/增强材料 | |
| 特性 | |
| 用途 | |
| 机构评级 | |
| RoHS 合规性 | |
| 外观 | |
| 形式 | |
| 加工方法 |
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 密度 | 1.64 | -- | g/cm3 | ISO 1183 |
| 收缩率 | 0.10 到 0.30 | -- | % | ISO 294-4 |
| 吸水率(23°C, 24 hr) | 0.16 | -- | % | ISO 62 |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 拉伸模量 | 19500 | 19500 | MPa | ISO 527-2 |
| 拉伸应力(断裂) | 280 | 260 | MPa | ISO 527-2 |
| 拉伸应变(断裂) | 1.9 | 2.2 | % | ISO 527-2 |
| 弯曲模量 | 18500 | -- | MPa | ISO 178 |
| 弯曲应力 | 380 | -- | MPa | ISO 178 |
| 冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 悬壁梁缺口冲击强度 | 110 | -- | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 | 850 | -- | J/m | ASTM D256 |
| 热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 热变形温度(1.8 MPa, 未退火) | 230 | -- | °C | ISO 75-2/A |
| 线形热膨胀系数 - 流动 | 1.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| 补充信息 | 干燥 | 调节后的 | ||
|---|---|---|---|---|
| 吸水性 - Equil, 65% RH | -- |
| 注射 | 干燥 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 120 | °C | |
| 干燥时间 | 0.50 到 1.5 | hr | |
| 料筒后部温度 | 250 到 260 | °C | |
| 料筒前部温度 | 260 到 290 | °C | |
| 射嘴温度 | 260 到 290 | °C | |
| 加工（熔体）温度 | 280 | °C | |
| 模具温度 | 120 到 140 | °C | |
| 注射速度 | 快速 |