PC/PBT XENOY X4850

Physical Properties	Metric	English	Comments
Specific Gravity	1.31g/cc	1.31g/cc	ASTM D792
Density	1.31g/cc	0.0473lb/in?3	ISO 1183
Moisture Absorption	0.140 %	0.140 %	23?°C / 50% RH; ISO 62
Water Absorption at Saturation	0.42 %	0.42 %	ISO 62
Linear Mold Shrinkage, Flow	0.0070-0.0090cm/cm @Thickness 3.20 mm	0.0070-0.0090in/in @Thickness 0.126 in	SABIC Method
Melt Flow	4.5g/10 min @Load 5.00 kg, Temperature 266 ?°C	4.5g/10 min @Load 11.0 lb, Temperature 511 ?°F	ASTM D1238
Melt Index of Compound	4.0g/10 min @Load 5.00 kg, Temperature 265 ?°C	4.0g/10 min @Load 11.0 lb, Temperature 509 ?°F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, H358/30	105MPa	15200psi	ISO 2039-1
Tensile Strength at Break	45.0MPa	6530psi	50 mm/min; ISO 527
	50.0MPa	7250psi	5 mm/min; ISO 527
	55.0MPa	7980psi	Type I, 50 mm/min; ASTM D638
	60.0MPa	8700psi	Type I, 5 mm/min; ASTM D638

PC/PBT XENOY X4850

简介：

PC-PBT 是PC与PBT的共混材料，通常以共混造料后，以粒料形状供应。如果只把两种料简单的混合后，直接注塑，效果很差，会出现分层现象

PC的优点是室温刚而韧，但高温的情况下，热变形严重。缺点是应力开裂，粘度大；PBT的优点是它的刚性不受温度的影响，变形小；这样共混后的材料PC-PBT即保留了两者的优点

PC-PBT具有较高的表面硬度，较高的刚性和韧性，也有较高的抗高温形的能力，也有较高的抗应力开裂能力；它的机械性能介于两者之间

抗高温变形对于大型的外壳类材料具有重要的意义。

产品特性：

·高韧性（即使在低温环境中）

·良好的耐化学品性能

·不易发生应力开裂

·良好的涂覆性能

·低吸湿率

用途：

·汽车工程

·电气工程/电子

·照明技术

·运动和休闲