东莞市宏阔塑胶有限公司
Eastman DuraStar DS2000 Polymer, Natural
Polymer,Thermoplastic,Polyester, TP,Polycyclohexylenedimethylene Terephthalate (PCT),Glycol-Modified PCT (PCTG) Copolyester
Eastman Chemical
产品说明:
Durastar DS2000 polymer has excellent appearance and is nearly water-clear. Its most outstanding features are toughness, chemical resistance, and excellent processing characteristics. DS2000 has very good toughness as shown by Izod impact resistance. Exposure to aromatic oils often causes crazing or actual fracture of many polymer resins, but DS2000 maintains its physical properties when exposed to these oils, and its appearance is virtually unchanged. Easy to process, it flows readily and fills intricate molds. Under existing United States Food and Drug Administration (FDA) regulations, Durastar DS2000 may be used in food contact articles which comply with the specifications and conditions of use in 21 CFR 177.1240.
Applications/Uses
- Point of purchase displays
- Toys/Sporting goods
- Writing instruments
- Good chemical resistance
- Excellent flow
- Outstanding impact resistance
- Excellent clarity
- Fast drying times
- Quick cycle times
Key Attributes
Eastman DuraStar DS2000 Polymer, Natural 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| 密度 | 1.19 g/cc | 0.0430 lb/in3 | ISO 1183 |
| 线性成型收缩率 | 0.0020 - 0.0060 cm/cm
@Thickness 3.20 mm
|
0.0020 - 0.0060 in/in
@Thickness 0.126 in
|
ASTM D955 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | 105 | 105 | ASTM D785 |
| 抗张强度(断裂) | 49.0 MPa | 7110 psi | ISO 527 |
| 53.0 MPa | 7690 psi | ASTM D638 | |
| 抗张强度(屈服) | 46.0 MPa | 6670 psi | ASTM D638 |
| 47.0 MPa | 6820 psi | ISO 527 | |
| 伸长率 (断裂) | 210 % | 210 % | ISO 527 |
| 310 % | 310 % | ASTM D638 | |
| 屈服伸长率 | 4.0 % | 4.0 % | ISO 527 |
| 5.0 % | 5.0 % | ASTM D638 | |
| 弯曲强度 | 64.0 MPa | 9280 psi | ISO 178 |
| 67.0 MPa | 9720 psi | ASTM D790 | |
| 弯曲模量 | 1.75 GPa | 254 ksi | ISO 178 |
| 1.90 GPa | 276 ksi | ASTM D790 | |
| 悬壁梁缺口冲击强度 | 0.600 J/cm
@Temperature -40.0 °C
|
1.12 ft-lb/in
@Temperature -40.0 °F
|
ASTM D256 |
| 3.70 J/cm
@Temperature 23.0 °C
|
6.93 ft-lb/in
@Temperature 73.4 °F
|
ASTM D256 | |
| 悬壁梁无缺口冲击强度 | NB | NB | ASTM D4812 |
| NB
@Temperature -40.0 °C
|
NB
@Temperature -40.0 °F
|
ASTM D4812 | |
| 悬壁梁缺口冲击强度 | 6.30 kJ/m2
@Temperature -40.0 °C
|
3.00 ft-lb/in2
@Temperature -40.0 °F
|
ISO 180 |
| 29.6 kJ/m2
@Temperature 23.0 °C
|
14.1 ft-lb/in2
@Temperature 73.4 °F
|
ISO 180 | |
| 多轴向仪器化冲击能量 | 45.0 J | 33.2 ft-lb | Puncture Resistance @Max Load, 23°C; ASTM D3763 |
| 71.0 J | 52.4 ft-lb | Puncture Resistance @ max load, 23°C; ISO 6603-2 | |
| 48.0 J
@Temperature -40.0 °C
|
35.4 ft-lb
@Temperature -40.0 °F
|
Puncture Resistance at Max Load; ASTM D3763 | |
| 55.0 J
@Temperature -40.0 °C
|
40.6 ft-lb
@Temperature -40.0 °F
|
Puncture Resistance at Max Load; ISO 6603-2 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(0.46 MPa) | 73.0 °C | 163 °F | ISO 75 |
| 73.0 °C | 163 °F | ASTM D648 | |
| 载荷下热变形温度(1.8 MPa) | 65.0 °C | 149 °F | ASTM D648 |
| 66.0 °C | 151 °F | ISO 75 | |
| 可燃性(UL94) | HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 雾度 | 0.30 % | 0.30 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | Regular Transmittance; ASTM D1003 |
| 91 % | 91 % | Total Transmittance; ASTM D1003 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 250 - 290 °C | 482 - 554 °F | |
| 模具温度 | 15.0 - 30.0 °C | 59.0 - 86.0 °F | |
| 干燥温度 | 70.0 °C | 158 °F | |
| 干燥时间 | 3 hour | 3 hour |
PCTA
PCTA是一种共聚聚酯塑料原料。具有高透明度，良好的韧性和冲击强度，优异的低温韧性，高抗撕性及良好的加工性能，优异的耐化学性能，可电镀，喷油，抗刮花，密度比PC低16%，加工成本比PC低40%，印刷、著色、电镀性能佳，韧性比透明ABS高3倍，符合欧洲RoHS环保指令，适用于高档次的化妆品，电子电气内材．玩具，高档笔，并可取代PC在各种领域内的运用。可采取传统的挤出、注塑、吹塑及吸塑等成型方法进行加工。广泛应用于板片材、高性能收缩膜、瓶用及异型材市场；可以用来生产玩具、家用器皿及医疗用品等。
简介
PCTA共聚物是环己烷二甲醇和对苯二酸，以及根据需要用别的酸部分取代对苯一酸所形成的聚合物。与PET相比具有较低的可萃取性，更好的耐热性，低温抗冲击性和水解稳定性。可应用于取向和流延薄膜、热成型盘子和单丝等领域。正常的PCTA共聚酯挤塑薄膜特性有：极亮的透明度、好的低温韧性、高抗撕性和耐化学性。在合成PCTA共聚酯时改变酸的比例可使聚合物具有不同的独特性质。例如可具有高结晶熔融温度(545F)，用于制作可烘烤盘子。PCTA还可以与其它聚酯共混或填充玻纤、云母，以满足各种性能要求。PCTA共聚酯制品可用于与食品接触的各种用途，这在FDA规范21CFR—177—12401中已有规定，并也得到USDA许可用作肉禽类包装材料。原料供应商以美国伊士曼为主。
伊士曼PCTA-DS2000
PCTG共聚酯与其他聚合物的熔融共混物提供了一定范围力学性能和热性能,可改性 后作为专门用途.PCTG共聚酯,表现出*的透明度和光学特性,如很好的透光性和很 低的混浊度,好的耐化学性和柔韧性,其缺口悬臂梁式冲击强度测定值高。通常熔体共 混物具有的性能与PC及其他PC为基础的共混物相近。以PCT和PCTG共聚酯为基础的熔体 共混物可具有比PC更好的耐某些化学物的性质,并表现出很好的光泽度和可着色性。 典型应用范围 电器/电子业,汽车,医药业,仪表器械,光学,游乐/专用车辆等.