东莞市常平浩云塑胶经营部
Borstar BB2581 HDPE
Borstar CB9600 HDPE
Borstar FB1460 HDPE
Borstar FB1520 HDPE
Borstar FB3450 HDPE
Borstar FB7400 HDPE
Borstar HE3410 HDPE
Borstar HE3470-LS HDPE
Borstar HE3474-LS HDPE
Borstar HE3476-LS HDPE
Borstar HE3477-LS HDPE
Borstar HE3490-IM HDPE
Borstar HE3490-LS HDPE
Borstar HE3492-LS HDPE
Borstar HE3494-LS HDPE
Borstar HE3495-LS HDPE
Borstar HE3496-LS HDPE
Borstar HE3497-LS HDPE
Borstar HE3498-LS HDPE
Borstar HE6061 HDPE
Borstar HE6062 HDPE
Borstar HE6063 HDPE
Borstar HE6067 HDPE
Borstar HE6068 HDPE
Borstar HE6081 HDPE
Borstar MB6561 HDPE
Borstar MB6562 HDPE
Borstar MB7541 HDPE
Borstar MB7542 HDPE
Borstar HE6063
高密度聚乙烯
Borealis AG
产品说明:
Borstar HE6063 is a natural, UV-stabilised, colourable, bimodal high density (HD) jacketing compound, which is produced with the Borealis proprietary Borstar bimodal process technology.
Borstar technology allows the manufacturing of polymers outside the traditional MFR and density range making it possible to optimize processability, reduce shrinkage and yet provide excellent physical toughness and environmental stress crack resistance (ESCR).
Borstar HE6063 contains a well dispersed UV-stabiliser in sufficient amount providing a measure of weathering resistance. In order to fully utilise the unique low shink properties of Borstar HE6063 we recommend the use of non-warping colour masterbatches.
The physical toughness and very low water permeability of the compound make it an ideal solution especially for buried power cables. Borstar HE6063 offers a balance of properties giving advantages in manufacturing, installation and lifetime performance of communication and energy cables.
Borstar HE6063 meets the applicable requirements as below when processed using sound extrusion practice and testing procedure:
Borstar technology allows the manufacturing of polymers outside the traditional MFR and density range making it possible to optimize processability, reduce shrinkage and yet provide excellent physical toughness and environmental stress crack resistance (ESCR).
Borstar HE6063 contains a well dispersed UV-stabiliser in sufficient amount providing a measure of weathering resistance. In order to fully utilise the unique low shink properties of Borstar HE6063 we recommend the use of non-warping colour masterbatches.
The physical toughness and very low water permeability of the compound make it an ideal solution especially for buried power cables. Borstar HE6063 offers a balance of properties giving advantages in manufacturing, installation and lifetime performance of communication and energy cables.
Borstar HE6063 meets the applicable requirements as below when processed using sound extrusion practice and testing procedure:
- ASTM D 1248 Type III, Class A, Category 4, Grade E9, J5
- BS 6234: Type H03, TS2
- DIN 57818/VDE 0818
- EN 50290-2-24
- D 620 S1, Part 1, table 4B, DMP 5, 13, 16
- IEC 60502, Type ST7
- IEC 60840, Type ST7
- ISO 1872-PE, KHLN, 45 D-006
- NF C32-060
Borstar HE6063 物性表
基本信息 | |
---|---|
添加剂 |
|
特性 |
|
用途 |
|
机构评级 |
|
外观 |
|
形式 |
|
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
密度1(基体树脂) | 0.946 | g/cm3 | ISO 1183 |
熔流率(熔体流动速率) | ISO 1133 | ||
190°C/2.16 kg | 0.50 | g/10 min | ISO 1133 |
190°C/5.0 kg | 2.0 | g/10 min | ISO 1133 |
抗环境应力开裂(条件 B, 50°C, 10% Igepal, F0) | 5000 | hr | IEC 60811-4-1/B |
硬度 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
肖氏硬度 | |||
邵氏 D, 1 秒 | 61 | ISO 868 | |
邵氏 D, 3 秒 | 60 | DIN 53505 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸应力(屈服) | 35.0 | MPa | ISO 527-2/50 |
拉伸应变(断裂) | 900 | % | ISO 527-2/50 |
弯曲模量 | 850 | MPa | ASTM D790 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
脆化温度 | -76.0 | °C | ASTM D746 |
电气性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
体积电阻率 | 10 | ohms·cm | IEC 60093 |
介电强度 | 70 | kV/mm | IEC 60243-1 |
补充信息 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
Pressure Test2(115°C) | % | IEC 60811-3-1 |
挤出 | 额定值 | 单位制 | |
---|---|---|---|
熔体温度 | 180 到 190 | °C |
挤压说明 |
---|
Preheating: 90 °CCooling water: 60 °C |
备注 | |
---|---|
1 . | ISO 1872-2 |
2 . | at high temperature, 6 hrs |