Eastman Eastar AN014 Copolyester
Polymer,Thermoplastic,Polyester, TP
Eastman Chemical
产品说明:
Eastar AN014 copolyester is a high flow product that contains a mold release. Eastar AN014 flow lengths are increased 20-40% relative to Eastar AN004 as shown by spiral flow testing. Other outstanding features of Eastar are easily maintained such as excellent appearance and clarity, good physical properties, chemical resistance, and easy processing. This high flow product is especially suited for those applications utilizing thin-walled intricate tools. Under existing United States Food and Drug Administration (FDA) regulations, Eastar AN014 may be used in food contact articles which comply with the specifications and conditions of use in 21 CFR 177.1240.
Applications/Uses
- Cosmetics/personal care packaging
- Fragrance packaging
Eastman Eastar AN014 Copolyester 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| 吸水率 | 0.15 % | 0.15 % | 24h Immersion; ASTM D570 |
| 线性成型收缩率 | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | 107 | 107 | ASTM D785 |
| 抗张强度(断裂) | 43.0 MPa | 6240 psi | ASTM D638 |
| 抗张强度(屈服) | 50.0 MPa | 7250 psi | ASTM D638 |
| 伸长率 (断裂) | 270 % | 270 % | ASTM D638 |
| 屈服伸长率 | 5.0 % | 5.0 % | ASTM D638 |
| 弯曲强度 | 68.0 MPa | 9860 psi | ASTM D790 |
| 弯曲模量 | 1.90 GPa | 276 ksi | ASTM D790 |
| 悬壁梁缺口冲击强度 | 0.440 J/cm
@Temperature -40.0 °C
|
0.824 ft-lb/in
@Temperature -40.0 °F
|
ASTM D256 |
| 0.800 J/cm
@Temperature 23.0 °C
|
1.50 ft-lb/in
@Temperature 73.4 °F
|
ASTM D256 | |
| 悬壁梁无缺口冲击强度 | NB | NB | ASTM D4812 |
| NB
@Temperature -40.0 °C
|
NB
@Temperature -40.0 °F
|
ASTM D4812 | |
| 多轴向仪器化冲击能量 | 40.0 J | 29.5 ft-lb | Puncture Resistance @Max Load, 23°C; ASTM D3763 |
| 38.0 J
@Temperature -40.0 °C
|
28.0 ft-lb
@Temperature -40.0 °F
|
Puncture Resistance at Max Load; ASTM D3763 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(0.46 MPa) | 73.0 °C | 163 °F | ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 66.0 °C | 151 °F | ASTM D648 |
| 维卡软化温度 | 86.0 °C | 187 °F | 1kg load; ASTM D1525 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 雾度 | = 1.0 % | = 1.0 % | ASTM D1003 |
| Transmission, Visible | 92 % | 92 % | Total Transmittance; ASTM D1003 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 230 - 280 °C | 446 - 536 °F | |
| 模具温度 | 15.0 - 30.0 °C | 59.0 - 86.0 °F | |
| 干燥温度 | 70.0 °C | 158 °F | |
| 干燥时间 | 4 hour | 4 hour |
Eastar an014共聚酯是一种含脱模剂的高流动性产品。螺旋流试验表明，eastar an014的流量长度比 eastar an004增加了20-40% 。其他突出的特点易于维护，如良好的外观和透明度，良好的物理性能，耐化学性，易于加工。这种高流量的产品特别适合于那些使用薄壁复杂工具的应用。根据现行美国食物及药物管理局(fda)规例，eastar an014可用于符合21 cfr 177.1240所载规格及使用条件的食物接触物品。用途/用途/化妆品/个人护理包装/香料包装
PCTA乙二醇改性-聚对苯二甲酸乙二醇酯,是一种高透明的共聚聚酯塑料原料。具有高透明度，水一般透明；韧性特高、耐冲击、弯曲；优异的耐化学腐蚀性能；良好的抗刮伤性；良好的加工性（流动性高，优异的着色性能，可进行丝印、喷油、电镀），高抗撕性及良好的加工性能，优异的耐化学性能。可采取传统的挤出、注塑、吹塑及吸塑等成型方法进行加工。密度：1.34g/cm3、热变形温度70℃。
广泛应用于板片材、高性能收缩膜、瓶用及异型材市场；可以用来生产玩具、家用器皿及医疗用品等；通过了美国FDA关于食品接触标准。 可以应用于医药包装及医疗透明配件，牙刷及个人护理品，笔及文具，家电及小家电的透明件，玩具、日用品、灯饰食品、医药、化妆品包装等领域。