东莞市宏阔塑胶有限公司
Eastman Eastar BR203 Copolyester
Polymer,Thermoplastic,Polyester, TP
Eastman Chemical
产品说明:
Eastar BR203 Copolyester contains a mold release additive. It has excellent appearance and is nearly water-clear. Its most outstanding features are its chemical resistance and processing capabilities. Exposure to aromatic oils often causes crazing or actual fracture of many polymer resins, but BR203 maintains its physical properties when exposed to these oils, and its appearance is virtually unchanged. BR203 is specifically formulated to provide the optimal combination of chemical resistance, bristle retention, strength, stiffness, toughness, processability, clarity, colorability, and feel for toothbrushes. Under existing United States Food and Drug Administration (FDA) regulations, Eastar BR203 copolyester may lawfully be used to make food contact articles which comply with the specifications and conditions of use in 21 CFR 177.1240.
Toothbrushes
Applications/Uses
Eastman Eastar BR203 Copolyester 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| 密度 | 1.19 g/cc | 0.0430 lb/in3 | ISO 1183 |
| 线性成型收缩率 | 0.0020 - 0.0060 cm/cm
@Thickness 3.20 mm
|
0.0020 - 0.0060 in/in
@Thickness 0.126 in
|
ASTM D955 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | 105 | 105 | ASTM D785 |
| 抗张强度(断裂) | 49.0 MPa | 7110 psi | ISO 527 |
| 53.0 MPa | 7690 psi | ASTM D638 | |
| 抗张强度(屈服) | 46.0 MPa | 6670 psi | ASTM D638 |
| 47.0 MPa | 6820 psi | ISO 527 | |
| 伸长率 (断裂) | 210 % | 210 % | ISO 527 |
| 310 % | 310 % | ASTM D638 | |
| 屈服伸长率 | 4.0 % | 4.0 % | ISO 527 |
| 5.0 % | 5.0 % | ASTM D638 | |
| 弯曲强度 | 64.0 MPa | 9280 psi | ISO 178 |
| 67.0 MPa | 9720 psi | ASTM D790 | |
| 弯曲模量 | 1.75 GPa | 254 ksi | ISO 178 |
| 1.90 GPa | 276 ksi | ASTM D790 | |
| 悬壁梁缺口冲击强度 | 0.600 J/cm
@Temperature -40.0 °C
|
1.12 ft-lb/in
@Temperature -40.0 °F
|
ASTM D256 |
| 3.70 J/cm
@Temperature 23.0 °C
|
6.93 ft-lb/in
@Temperature 73.4 °F
|
ASTM D256 | |
| 悬壁梁无缺口冲击强度 | NB | NB | ASTM D4812 |
| NB
@Temperature -40.0 °C
|
NB
@Temperature -40.0 °F
|
ASTM D4812 | |
| 悬壁梁缺口冲击强度 | 6.30 kJ/m2
@Temperature -40.0 °C
|
3.00 ft-lb/in2
@Temperature -40.0 °F
|
ISO 180 |
| 29.6 kJ/m2
@Temperature 23.0 °C
|
14.1 ft-lb/in2
@Temperature 73.4 °F
|
ISO 180 | |
| 多轴向仪器化冲击能量 | 45.0 J | 33.2 ft-lb | Puncture Resistance @Max Load, 23°C; ASTM D3763 |
| 71.0 J | 52.4 ft-lb | Puncture Resistance @ max load, 23°C; ISO 6603-2 | |
| 48.0 J
@Temperature -40.0 °C
|
35.4 ft-lb
@Temperature -40.0 °F
|
Puncture Resistance at Max Load; ASTM D3763 | |
| 55.0 J
@Temperature -40.0 °C
|
40.6 ft-lb
@Temperature -40.0 °F
|
Puncture Resistance at Max Load; ISO 6603-2 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(0.46 MPa) | 73.0 °C | 163 °F | ISO 75 |
| 73.0 °C | 163 °F | ASTM D648 | |
| 载荷下热变形温度(1.8 MPa) | 65.0 °C | 149 °F | ASTM D648 |
| 66.0 °C | 151 °F | ISO 75 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 雾度 | 0.30 % | 0.30 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | Regular Transmittance; ASTM D1003 |
| 91 % | 91 % | Total Transmittance; ASTM D1003 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 250 - 290 °C | 482 - 554 °F | |
| 模具温度 | 15.0 - 30.0 °C | 59.0 - 86.0 °F | |
| 干燥温度 | 70.0 °C | 158 °F | |
| 干燥时间 | 3 hour | 3 hour |
Eastar br203共聚酯含有脱模添加剂。它外观极佳，几乎是水清的。其最突出的特点是其耐化学性和加工能力。接触芳香油通常会导致许多聚合物树脂破裂，但 br203在接触这些油时保持其物理性能，其外观几乎没有改变。Br203是专门为牙刷的耐化学性、硬度、刚度、韧性、加工性、透明度、着色性和手感提供最佳组合的产品。根据现行的美国食品及药物管理局(fda)规例，eastar br203共聚酯可合法用于制造符合 cfr177.1240第21条规格及使用条件的食物接触物品。应用程序/usestoothbrush
1.PCTA牙刷柄用料/PCTA BR203/美国伊士曼/不含双酚A/符合口腔卫生标准原料/儿童牙刷用料，极高透明度，清晰度。PCTABR203透明度90%,加工成品晶莹剔透，色泽艳丽。
2.PCTABR203不含双酚A，加工成本比PC低40%，取代PC在各种领域内的运用。
3.PCTA牙刷柄用料/PCTA BR203/美国伊士曼/不含双酚A/符合口腔卫生标准原料/儿童牙刷用料/高韧性和良好的耐化学性对于侵蚀性强的牙膏及漱口水成分BR203也能显示出优良的耐化学性。
PCTA牙刷柄用料/PCTA BR203/美国伊士曼/不含双酚A/符合口腔卫生标准原料/儿童牙刷用料/高韧性在日常生活我们会用到很多塑胶类产品，作为和身体直接接触的用品，其安全性和***性必须有保障，PCTABR203食品级原料，环保***，低温下韧性足，避免因玩具破裂伤害儿童。PCTABR203加工性能***，可注塑成型成各种形态，着色性能好，脱模性能佳，可以加工生产各种形态模具，提升产品的多元化。