东莞市宏阔塑胶有限公司
Eastman Eastar AN004 Natural PCTA Copolyester
Polymer,Thermoplastic,Polyester, TP,PCTA Polyester Alloy,Polycyclohexylenedimethylene Terephthalate (PCT)
Eastman Chemical
产品说明:
EASTAR AN004 Copolyester contains a mold release. It has excellent appearance and is nearly water-clear. Its most outstanding features are its chemical resistance and processing capabilities. Exposure to aromatic oils often causes crazing or actual fracture of many polymer resins, but AN004 maintains its physical properties when exposed to these oils, and its appearance is virtually unchanged. Easy to process, it flows readily and fills intricate molds. Its processability coupled with its outstanding chemical resistance makes it well suited for thick-wall applications.
Applications:Floor care; Fragrance packaging; Housewares; Point of purchase displays; Refrigerator interior parts; Toys/Sporting goods; Writing instruments
Applications:Floor care; Fragrance packaging; Housewares; Point of purchase displays; Refrigerator interior parts; Toys/Sporting goods; Writing instruments
Properties reported here are typical of average lots. Eastman makes no representation that the material in any particular shipment will conform exactly to the values given.
Information provided by Eastman Chemical.
Eastman Eastar AN004 Natural PCTA Copolyester 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.20 g/cc | 0.0434 lb/in3 | ASTM D792 and ISO 1183 |
| 吸水率 | 0.13 % | 0.13 % | 24 hour immersion; ISO 62 |
| 线性成型收缩率,Flow | 0.0060 cm/cm
@Thickness 3.20 mm
|
0.0060 in/in
@Thickness 0.126 in
|
ASTM D955 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | 117 | 117 | ASTM D785 |
| 极限抗拉强度 | 56.0 MPa | 8120 psi | ISO 527 |
| 抗张强度(屈服) | 56.0 MPa | 8120 psi | ISO 527 |
| 伸长率 (断裂) | 130 % | 130 % | ISO 527 |
| 屈服伸长率 | 5.4 % | 5.4 % | ISO 527 |
| 弯曲强度 | 81.0 MPa | 11700 psi | ISO 178 |
| 弯曲模量 | 2.10 GPa | 305 ksi | ISO 178 |
| 悬壁梁缺口冲击强度 | NB | NB | ASTM D256 |
| 0.750 J/cm
@Temperature -40.0 °C
|
1.41 ft-lb/in
@Temperature -40.0 °F
|
ASTM D256 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 电阻率 | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| 表面电阻 | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| 介电常数 | 2.1
@Frequency 1e+6 Hz
|
2.1
@Frequency 1e+6 Hz
|
ASTM D 150 |
| 2.3
@Frequency 1000 Hz
|
2.3
@Frequency 1000 Hz
|
ASTM D150 | |
| 介电强度 | 17.3 kV/mm | 439 kV/in | Short Time, 500 V/sec rate-of-rise; ASTM D 149 |
| 耗散因数 | 0.0020
@Frequency 1000 Hz
|
0.0020
@Frequency 1000 Hz
|
ASTM D150 |
| 0.0080
@Frequency 1e+6 Hz
|
0.0080
@Frequency 1e+6 Hz
|
ASTM D150 | |
| 相比耐漏电起痕指数(CTI) | = 600 V | = 600 V | ASTM D3638 |
| 高压电弧跟踪率，HVTR | 38.0 mm/min | 1.50 in/min | UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比热容 | 1.38 J/g-°C
@Temperature 60.0 °C
|
0.330 BTU/lb-°F
@Temperature 140 °F
|
|
| 2.18 J/g-°C
@Temperature 240 °C
|
0.521 BTU/lb-°F
@Temperature 464 °F
|
||
| 载荷下热变形温度(0.46 MPa) | 103 °C | 217 °F | ASTM D648 and ISO 75 |
| 载荷下热变形温度(1.8 MPa) | 90.0 °C | 194 °F | ASTM D648 and ISO 75 |
| 维卡软化温度 | 110 °C | 230 °F | 5 kg load; ISO 306 |
| 118 °C | 244 °F | 1 kg load; ISO 306 | |
| 可燃性(UL94) | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
|
| V-2
@Thickness 3.20 mm
|
V-2
@Thickness 0.126 in
|
natural and white | |
| V-2
@Thickness 1.60 mm
|
V-2
@Thickness 0.0630 in
|
natural and white |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 雾度 | 3.6 % | 3.6 % | ASTM D1003 |
| Transmission, Visible | 77 % | 77 % | Regular transmittance per ASTM D 1003 |
| 81 % | 81 % | Total Transmittance; ASTM D 1003 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 280 °C | 536 °F | |
| 模具温度 | 47.5 °C | 118 °F | |
| 干燥温度 | 95.0 °C | 203 °F | |
| 干燥时间 | 6 hour | 6 hour |
Eastar an004共聚酯包含一个脱模剂。它外观极佳，几乎是水清的。其最突出的特点是其耐化学性和加工能力。接触芳香油通常会导致许多聚合物树脂破裂，但当接触这些油时，an004保持了它的物理性能，它的外观几乎没有改变。易于加工，易于流动，填充复杂的模具。它的可加工性和卓越的耐化学性使其非常适合厚壁应用。应用范围: 地板护理; 香水包装; 家庭用品; 购买点显示器; 冰箱内部零件; 玩具/运动产品; 书写工具/特性是一般批次的典型产品。Eastman 没有表示任何一批货物中的材料，将完全符合给定的价值。
PCTA共聚物是环己烷二甲醇和对苯二酸，以及根据需要用别的酸部分取代对苯一酸所形成的聚合物。PCTA 美国伊士曼 AN004 ,PCTA是一种共聚聚酯塑料原料。由环己烷二甲醇和对苯二酸构成。具有高透明度，良好的韧性和冲击强度，的低温韧性，高抗撕性及良好的加工性能，的耐化学性能，可电镀，喷油，抗刮花，密度比PC低16%，加工成本比PC低40%，印刷、著色、电镀性能佳，韧性比透明ABS高3倍，符合欧洲RoHS环保指令，适用于次的化妆品，电子电气内材．玩具，笔，并可取代PC在各种领域内的运用。可采取传统的挤出、注塑、吹塑及吸塑等成型进行加工。应用于板片材、收缩膜、瓶用及异型材市场；可以用来生产玩具、家用器皿及医疗用品等。