DURASTAR DS1010 polymer contains a mold release. It has excellent appearance and clarity. Its most outstanding features are chemical resistance and excellent processing characteristics. Exposure to aromatic oils often causes crazing or actual fracture of many polymer resins, but DS1010 maintains its physical properties when exposed to these oils, and its appearance is virtually unchanged. Easy to process, it flows readily, fills intricate molds, and is well suited for thick-wall applications. Under existing United States Food and Drug Administration (FDA) regulations, DURASTAR DS1010 may be used in food contact articles which comply with the specifications and conditions of use in 21 CFR 177.1240.

Applications:Appliances; Furniture/Furniture trim; Point of purchase displays; Toys/Sporting goods

Properties reported here are typical of average lots. Eastman makes no representation that the material in any particular shipment will conform exactly to the values given.

Information provided by Eastman Chemical.

Eastman DURASTAR DS1010 Natural PCTA Copolyester 物性表

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.20 g/cc	0.0434 lb/in3	ASTM D792
线性成型收缩率,Flow	0.0040 cm/cm @Thickness 3.20 mm	0.0040 in/in @Thickness 0.126 in	ASTM D955

机械性能	额定值 (公制)	额定值 (英制)	测试方法
洛氏硬度（R 级）	103	103	ASTM D785
极限抗拉强度	46.0 MPa	6670 psi	ISO 527
	51.0 MPa	7400 psi	ASTM D638
抗张强度(屈服)	47.0 MPa	6820 psi	ASTM D638 and ISO 527
伸长率 (断裂)	200 %	200 %	ISO 527
屈服伸长率	4.0 %	4.0 %	ISO 527
拉伸模量	1.80 GPa	261 ksi	ISO 527
弯曲强度	65.0 MPa	9430 psi	ISO 178
	69.0 MPa	10000 psi	ASTM D790
弯曲模量	1.85 GPa	268 ksi	ISO 178
悬壁梁缺口冲击强度	0.800 J/cm	1.50 ft-lb/in	ASTM D256
	0.400 J/cm @Temperature -40.0 °C	0.749 ft-lb/in @Temperature -40.0 °F	ASTM D256

热性能	额定值 (公制)	额定值 (英制)	测试方法
载荷下热变形温度(0.46 MPa)	73.0 °C	163 °F	ASTM D648
载荷下热变形温度(1.8 MPa)	65.0 °C	149 °F	ASTM D648

光学性能	额定值 (公制)	额定值 (英制)	测试方法
雾度	0.30 %	0.30 %	ASTM D1003
Transmission, Visible	89 %	89 %	Regular transmittance per ASTM D 1003
	91 %	91 %	Total Transmittance; ASTM D 1003

加工性能	额定值 (公制)	额定值 (英制)	测试方法
加工（熔体）温度	255 °C	491 °F
模具温度	22.5 °C	72.5 °F
干燥温度	70.0 °C	158 °F

Durastar ds1010聚合物包含一个脱模剂。它的外观和清晰度都很好。其最突出的特点是耐化学腐蚀性和优良的加工性能。接触芳香油通常会导致许多聚合物树脂开裂或实际断裂，但 ds1010在接触这些油时保持其物理性能，其外观几乎没有改变。易于加工，易于流动，填充复杂的模具，非常适合厚壁应用。根据现行的美国食物及药物管理局(fda)规例，杜拉斯达 ds1010可用于符合21 cfr 177.1240所载规格及使用条件的食物接触物品。应用: 电器; 家具/家具装饰; 购买地点展示; 玩具/运动商品/特性报告在这里是典型的平均批量。Eastman 没有表示任何一批货物中的材料，将完全符合给定的价值。

简介

PCTA共聚物是环己烷二甲醇和对苯二酸，以及根据需要用别的酸部分取代对苯一酸所形成的聚合物。与PET相比具有较低的可萃取性，更好的耐热性，低温抗冲击性和水解稳定性。可应用于取向和流延薄膜、热成型盘子和单丝等领域。正常的PCTA共聚酯挤塑薄膜特性有：极亮的透明度、好的低温韧性、高抗撕性和耐化学性。在合成PCTA共聚酯时改变酸的比例可使聚合物具有不同的性质。例如可具有高结晶熔融温度(545F)，用于制作可烘烤盘子。PCTA还可以与其它聚酯共混或填充玻纤、云母，以满足各种性能要求。PCTA共聚酯制品可用于与食品接触的各种用途，这在FDA规范21CFR—177—12401中已有规定，并也得到USDA许可用作肉禽类包装材料。原料供应商以美国伊士曼为主。

PCTA是一种共聚聚酯塑料原料。具有高透明度，良好的韧性和冲击强度，优 异的低温韧性，高抗撕性及良好的加工性能，优 异的耐化学性能，可电镀，喷油，抗刮花，密度比PC低16%，加工成本比PC低40%，印刷、著色、电镀性能佳，韧性比透明ABS高3倍，符合欧洲RoHS环保指令，适用于高 档 次的化妆品，电子电气内材．玩具，笔，并可取代PC在各种领域内的运用。可采取传统的挤出、注塑、吹塑及吸塑等成型进行加工。广 泛应用于板片材、收缩膜、瓶用及异型材市场；可以用来生产玩具、家用器皿及医疗用品等。