东莞市宏阔塑胶有限公司
Tritan? TX1001
共聚多酯
Eastman Chemical Company
产品说明：
Eastman Tritan? TX1001 is an amorphous copolyester with excellent appearance and clarity. EastmanTritan? TX1001 contains a mold release derived from vegetable based sources. Its most outstanding features are excellent toughness, hydrolytic stability, and heat and chemical resistance. This new-generation copolyester can also be molded into various applications without incorporating high levels of residual stress. Combined with Tritan? copolyester"s outstanding chemical resistance and hydrolytic stability, these features give molded products enhanced durability in the dishwasher environment, which can expose products to high heat, humidity and aggressive cleaning detergents. Tritan? TX1001 copolyester may be used in repeated use food contact articles under United States Food and Drug Administration (FDA) regulations. Tritan? TX1001 copolyester is certified to NSF/ANSI Standard 51 for Food Equipment Materials and is also certified to NSF/ANSI Standard 61 - Drinking Water System Components-Health Effects.
Tritan? TX1001 物性表
| 基本信息 | |
|---|---|
| 黄卡编号 | |
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.18 | g/cm3 | ASTM D792 |
| 收缩率 - 流动 | 0.50 到 0.70 | % | ASTM D955 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度(R 级, 23°C) | 112 | ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量(23°C) | 1550 | MPa | ASTM D638, ISO 527-2 |
| 抗张强度 | |||
| 屈服, 23°C | 43.0 | MPa | ASTM D638, ISO 527-2 |
| 断裂, 23°C | 53.0 | MPa | ASTM D638 |
| 断裂, 23°C | 58.0 | MPa | ISO 527-2 |
| 伸长率 | |||
| 屈服, 23°C | 6.0 | % | ASTM D638 |
| 屈服, 23°C | 7.0 | % | ISO 527-2 |
| 断裂, 23°C | 210 | % | ASTM D638 |
| 断裂, 23°C | 190 | % | ISO 527-2 |
| 弯曲模量 | |||
| 23°C | 1550 | MPa | ASTM D790 |
| 23°C | 1500 | MPa | ISO 178 |
| 弯曲应力 | |||
| 23°C | 59.0 | MPa | ISO 178 |
| 屈服, 23°C | 62.0 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 | |||
| 23°C | 980 | J/m | ASTM D256 |
| -40°C | 20 | kJ/m2 | ISO 180 |
| 23°C | 93 | kJ/m2 | ISO 180 |
| 无缺口悬臂梁冲击(23°C) | 无断裂 | ASTM D4812 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火 | 99.0 | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 85.0 | °C | ASTM D648 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 透射率(总计) | 90.0 | % | ASTM D1003 |
| 雾度 | 1.0 | % | ASTM D1003 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 88.0 | °C | |
| 干燥时间 | 4.0 到 6.0 | hr | |
| 加工（熔体）温度 | 260 到 282 | °C | |
| 模具温度 | 38.0 到 66.0 | °C |
伊士曼 triantm tx1001是一种无定形的共聚酯具有出色的外观和清晰度。1001包含了从蔬菜中提取的霉菌释放物。其最突出的特点是优良的韧性，水解稳定性，耐热和耐化学品。这种新一代的共聚酯也可以被塑造成各种应用，而无需纳入高水平的残余应力。结合 triantm 共聚酯优异的化学防腐剂
用途:电子电器,家用电器,家用日杂,食品级
特性备注:共聚物;抗撞击性,高;可加工性,良好;快的成型周期;耐化学性良好;耐热性,高;耐用性;清晰度,高;韧性良好;食品接触的合规性;水解稳定;脱模性能良好;外观良好;无定形的
重要参数:密度:1.18 g/cm3成型收缩率:0.5 %拉伸强度:43 MPa断裂伸长率:210 %弯曲强度:59 MPa弯曲模量:1500 MPa硬度:112热变形温度:99 ℃
PCTA共聚酯与其他聚合物的熔融共混物提供了一定范围力学性能和热性能,可改性 后作为专门用途.PCTA共聚酯,表现出*的透明度和光学特性,如很好的透光性和很 低的混浊度,好的耐化学性和柔韧性,其缺口悬臂梁式冲击强度测定值高。通常熔体共 混物具有的性能与PC及其他PC为基础的共混物相近。以PCT和PCTA共聚酯为基础的熔体 共混物可具有比PC更好的耐某些化学物的性质,并表现出很好的光泽度和可着色性。 典型应用范围 电器/电子业,汽车,医药业,仪表器械,光学,游乐/专用车辆等.