东莞市金灿塑胶新材料有限公司
PA6 德国巴斯夫 6030G HS BK 注塑级/电器外壳;薄膜
| 颜色 | |
| 特性 | 耐油;高抗冲 |
| 应用领域 | 电器外壳;薄膜 |
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
|---|---|---|---|---|
| 密度 / 比重 | ASTMD792 | 1.13 | g/cm3 | |
| ISO1183 | 1.13 | g/cm3 | ||
| 收缩率 | MD：3.18mm | 0.90 | % | |
| 吸水率 | 24hr | ASTMD570 | 1.6 | % |
| 23°C,24hr | ISO62 | 1.6 | % | |
| 饱和 | ASTMD570 | 9.3 | % | |
| 饱和,23°C | ISO62 | 9.3 | % | |
| 平衡,50%RH | ASTMD570 | 2.6 | % | |
| 平衡,23°C,50%RH | ISO62 | 2.6 | % | |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 标称拉伸断裂应变 | -40°C | ISO527-2 | 5.0 | % |
| 23°C | ISO527-2 | 7.0 | % | |
| 80°C | ISO527-2 | 100 | % | |
| 120°C | ISO527-2 | 100 | % | |
| 断裂伸长率 | ASTM D638/ISO 527 | 50 | % | |
| 抗张强度 | 屈服,-40°C | ASTMD638 | 137 | Mpa |
| 屈服,23°C | ASTMD638 | 90.0 | Mpa | |
| 屈服,80°C | ASTMD638 | 40.0 | Mpa | |
| Yield,121°C | ASTMD638 | 30.0 | Mpa | |
| 断裂,-40°C | ASTMD638 | 130 | Mpa | |
| 断裂,23°C | ASTMD638 | 90.0 | Mpa | |
| 断裂,80°C | ASTMD638 | 35.0 | Mpa | |
| Break,121°C | ASTMD638 | 25.0 | Mpa | |
| 拉伸模量 | -40°C | ISO527-2 | 4090 | Mpa |
| 23°C | ISO527-2 | 3700 | Mpa | |
| 80°C | ISO527-2 | 750 | Mpa | |
| 120°C | ISO527-2 | 550 | Mpa | |
| 150°C | ISO527-2 | 445 | Mpa | |
| 拉伸应变 | 屈服,23°C | ISO527-2 | 4.0 | % |
| 拉伸应力 | 屈服,-40°C | ISO527-2 | 137 | Mpa |
| 屈服,23°C | ISO527-2 | 88.0 | Mpa | |
| 屈服,80°C | ISO527-2 | 40.0 | Mpa | |
| 屈服,120°C | ISO527-2 | 30.0 | Mpa | |
| 屈服,150°C | ISO527-2 | 25.0 | Mpa | |
| 洛氏硬度 | ASTM D785 | 120 | ||
| 伸长率 | 屈服,-40°C | ASTMD638 | 3.0 | % |
| 屈服,23°C | ASTMD638 | 4.0 | % | |
| 屈服,80°C | ASTMD638 | 25 | % | |
| Yield,121°C | ASTMD638 | 27 | % | |
| 断裂,23°C | ASTMD638 | 12 | % | |
| 断裂,80°C | ASTMD638 | 100 | % | |
| Break,121°C | ASTMD638 | 100 | % | |
| 断裂,-40°C | ASTMD638 | 5.0 | % | |
| 弯曲模量 | -40°C | ASTMD790 | 3370 | Mpa |
| 23°C | ASTMD790 | 3170 | Mpa | |
| 65°C | ASTMD790 | 600 | Mpa | |
| 90°C | ASTMD790 | 440 | Mpa | |
| 121°C | ASTMD790 | 385 | Mpa | |
| 23°C | ISO178 | 2800 | Mpa | |
| 弯曲强度 | -40°C | ASTMD790 | 183 | Mpa |
| 23°C | ASTMD790 | 110 | Mpa | |
| 65°C | ASTMD790 | 30.0 | Mpa | |
| 121°C | ASTMD790 | 21.0 | Mpa | |
| 弯曲应力 | 23°C | ISO178 | 95.0 | Mpa |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| RTIElec | 0.71mm | UL746 | 125 | °C |
| 1.5mm | UL746 | 125 | °C | |
| 3.0mm | UL746 | 125 | °C | |
| 6.0mm | UL746 | 125 | °C | |
| RTIImp | 0.71mm | UL746 | 65.0 | °C |
| 1.5mm | UL746 | 75.0 | °C | |
| 3.0mm | UL746 | 75.0 | °C | |
| 6.0mm | UL746 | 75.0 | °C | |
| RTIStr | 0.71mm | UL746 | 65.0 | °C |
| 1.5mm | UL746 | 85.0 | °C | |
| 3.0mm | UL746 | 85.0 | °C | |
| 6.0mm | UL746 | 85.0 | °C | |
| 燃烧性（率） | UL94 | V-2 | ||
| 热变形温度 | 0.45MPa,未退火 | ASTMD648 | 190 | °C |
| 0.45MPa,未退火 | ISO75-2/B | 165 | °C | |
| 1.8MPa,未退火 | ASTMD648 | 75.0 | °C | |
| 1.8MPa,未退火 | ISO75-2/A | 65.0 | °C | |
| 溶融温度（DSC） | ISO3146 | 220 | °C | |
| 熔融峰值温度 | ASTMD3418 | 220 | °C | |
| 线形热膨胀系数 | MD | ASTME831 | 8.1E-05 | cm/cm/°C |
| 电气性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| VolumeResistivity | 1.50mm | ASTMD257 | 1.0E 13 | ohms·cm |
| 介电强度2 | 1.50mm | ASTMD149 | 30 | KV/mm |
| 漏电起痕指数 | IEC60112 | 600 | V | |
| 体积电阻率 | IEC60093 | 1.0E 13 | ohms·cm | |
| 冲击性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 简支梁缺口冲击强度 | 23°C | ISO179 | 3.5 | kJ/m2 |
| 简支梁无缺口冲击强度 | 23°C | ISO179 | NoBreak | |
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 32 | J/m |
| 23°C | ASTMD256 | 48 | J/m | |
| 可燃性(Flammability) | 测试条件 | 测试方法 | 测试结果 | 单位 |
| UL阻燃等级 | 0.71mm | UL94 | V-2 | |
| 1.5mm | UL94 | V-2 | ||
| 3.0mm | UL94 | V-2 | ||
| 6.0mm | UL94 | V-2 | ||
| 硬度Hardness | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 洛氏硬度 | R级 | ASTMD785 | 120 | |
| 物性性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 比重（密度） | ASTM D792/ISO 1183 | 1.13 | ||
| 补充信息 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| DropWeightImpactStrength | 23°C | 内部方法 | 122 | J |