PA66 Zytel FR70M30V0 BK010
30% Mineral Reinforced, Flame Retardant, Polyamide 66
Information provided by DuPont. This product line has remained with DuPont after the DuPont-Dow merger.
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.62g/cc | 0.0585lb/in3 | DAM; ISO 1183 |
Linear Mold Shrinkage, Flow | 0.0080cm/cm | 0.0080in/in | DAM; ISO 294-4, 2577 |
Linear Mold Shrinkage, Transverse | 0.0090cm/cm | 0.0090in/in | DAM; ISO 294-4, 2577 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength at Break | 45.0MPa | 6530psi | 50% RH; ISO 527-1/-2 |
65.0MPa | 9430psi | DAM; ISO 527-1/-2 | |
Elongation at Break | 2.0 % | 2.0 % | DAM; ISO 527-1/-2 |
3.5 % | 3.5 % | 50% RH; ISO 527-1/-2 | |
Tensile Modulus | 4.00GPa | 580ksi | 50% RH; ISO 527-1/-2 |
6.20GPa | 899ksi | DAM; ISO 527-1/-2 | |
Poissons Ratio | 0.35 | 0.35 | DAM; ISO 527-1/-2 |
0.36 | 0.36 | 50%RH; ISO 527-1/-2 | |
Izod Impact, Unnotched (ISO) | 2.00kJ/m2 @Temperature 23.0 °C |
0.952ft-lb/in2 @Temperature 73.4 °F |
DAM; ISO 180/1A |
2.50kJ/m2 @Temperature 23.0 °C |
1.19ft-lb/in2 @Temperature 73.4 °F |
50% RH; ISO 180/1A |
PA66 Zytel FR70M30V0 BK010
PA特性
1、具有优良的耐磨性、自润滑性,机械强度较高。但吸水性较大,因而尺寸稳定性较差
2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性,其程度主要取决于材料的组成、壁厚以及环境条件。
3、在产品设计时,一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性,经常加入各种各样的改性剂。玻璃就是最常见的添加剂,有时为了提高抗冲击性还加入合成橡胶,如EPDM和SBR等。PA66的粘性较低,因此流动性很好(但不如PA6)。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。
4、PA66的收缩率在1%~2%之间,加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性,但对酸和其它一些氯化剂的抵抗力较弱。
PA66应用
高温电气插座零件、电气零件、齿轮、轴承、滚子、弹簧支架、滑轮、螺栓、叶轮、风扇叶片、螺旋桨、高压封口垫片、阀座、输油管、储油容器、绳索、扎带、传动皮带、砂轮粘合剂、电池箱、绝缘电气零件、线芯、抽丝等