东莞市宏阔塑胶有限公司
SABIC Innovative Plastics Xenoy? 5220U PBT+PC
Polymer,Thermoplastic,Polycarbonate (PC),Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced,Polyester, TP,Polybutylene Terephthalate (PBT)
SABIC Innovative Plastics (GE Plastics)
产品说明:
Unreinforced PBT+PC Alloy. Impact Modified. Improved retention of mechanical properties under UV exposure. Excellent low temperature impact and chemical resistance.
SABIC Innovative Plastics Xenoy? 5220U PBT+PC 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| 密度 | 1.22 g/cc | 0.0441 lb/in3 | ISO 1183 |
| 水分吸收 | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.50 % | 0.50 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0080 - 0.010 cm/cm
@Thickness 3.20 mm
|
0.0080 - 0.010 in/in
@Thickness 0.126 in
|
SABIC Method |
| 线性成型收缩率，横向 | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | on Tensile Bar; SABIC Method |
| 熔体流动速率 | 16 g/10 min
@Load 5.00 kg, Temperature 250 °C
|
16 g/10 min
@Load 11.0 lb, Temperature 482 °F
|
ISO 1133 |
| 化合物熔体指数 | 15 g/10 min
@Load 5.00 kg, Temperature 250 °C
|
15 g/10 min
@Load 11.0 lb, Temperature 482 °F
|
MVR [cm^3/10 min]; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
| 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 | |
| 抗张强度(屈服) | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
| 53.0 MPa | 7690 psi | Type I, 50 mm/min; ASTM D638 | |
| 伸长率 (断裂) | 120 % | 120 % | Type I, 50 mm/min; ASTM D638 |
| 120 % | 120 % | 50 mm/min; ISO 527 | |
| 屈服伸长率 | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 50 mm/min; ISO 527 | |
| 拉伸模量 | 2.05 GPa | 297 ksi | 1 mm/min; ISO 527 |
| 2.25 GPa | 326 ksi | 50 mm/min; ASTM D638 | |
| 2.25 GPa | 326 ksi | 5 mm/min; ASTM D638 | |
| 弯曲强度 | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
| 84.0 MPa | 12200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| 2.03 GPa | 294 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 悬壁梁缺口冲击强度 | 7.10 J/cm | 13.3 ft-lb/in | ASTM D256 |
| 2.99 J/cm
@Temperature -40.0 °C
|
5.60 ft-lb/in
@Temperature -40.0 °F
|
ASTM D256 | |
| 5.30 J/cm
@Temperature -30.0 °C
|
9.93 ft-lb/in
@Temperature -22.0 °F
|
ASTM D256 | |
| 50.0 kJ/m2 | 23.8 ft-lb/in2 | 80*10*4; ISO 180/1A | |
| 30.0 kJ/m2
@Temperature -30.0 °C
|
14.3 ft-lb/in2
@Temperature -22.0 °F
|
80*10*4; ISO 180/1A | |
| 简支梁缺口冲击强度 | 5.50 J/cm2 | 26.2 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 落锤总能量 | 60.0 J
@Temperature 23.0 °C
|
44.3 ft-lb
@Temperature 73.4 °F
|
ASTM D3763 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 耐电弧性 | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| 相比耐漏电起痕指数(CTI) | 400 - 600 V | 400 - 600 V | UL 746A |
| 热丝引燃 (HWI) | 15 - 30 sec | 15 - 30 sec | UL 746A |
| 高电弧燃烧，HAI | = 120 arcs | = 120 arcs | UL 746A |
| 高压电弧跟踪率，HVTR | 0.000 - 10.0 mm/min | 0.000 - 0.394 in/min | UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 95.0 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
52.8 μin/in-°F
@Temperature -40.0 - 104 °F
|
ASTM E 831 |
| 95.0 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
52.8 μin/in-°F
@Temperature -40.0 - 104 °F
|
ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | 90.0 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
50.0 μin/in-°F
@Temperature -40.0 - 104 °F
|
ASTM E 831 |
| 90.0 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
50.0 μin/in-°F
@Temperature -40.0 - 104 °F
|
ISO 11359-2 | |
| 载荷下热变形温度(0.46 MPa) | 107 °C
@Thickness 6.40 mm
|
225 °F
@Thickness 0.252 in
|
unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 75.0 °C | 167 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 84.0 °C
@Thickness 3.20 mm
|
183 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 | |
| 99.0 °C
@Thickness 6.40 mm
|
210 °F
@Thickness 0.252 in
|
unannealed; ASTM D648 | |
| 维卡软化温度 | 120 °C | 248 °F | Rate B/50; ISO 306 |
| 122 °C | 252 °F | Rate B/50; ASTM D1525 | |
| 125 °C | 257 °F | Rate B/120; ISO 306 | |
| UL RTI | 75.0 °C | 167 °F | UL 746B |
| UL RTI，机械冲击 | 75.0 °C | 167 °F | UL 746B |
| UL RTI，机械无冲击 | 75.0 °C | 167 °F | UL 746B |
| 可燃性(UL94) | HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
UL 94 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Specific Volume | 0.83cm^3/g | ASTM D792 |
| UV-light, water exposure/immersion | F2 | UL 746C |
PC，PBT，PC/PBT三者的关系以及区别：1.PC/PBT是PC与PBT的共混材料，通常以共混造料后，以粒料形状供应。如果只把两种料简单的混合后，直接注塑，效果很差，会出现分层现象。PC/PBT 基础创新塑料(美国)1731-WH9G145伴音输出变压器骨架热会变形严重尺寸安定性良好耐药品性、耐油性极佳pc对材料的抗热氧老化稳定性要求很高其成模周期往往为注塑方式的2至3倍电气性质优良可委托我司全权负责抗高温变形对于大形的外壳类材料具有重要的意义也有较高的抗应力开裂能力】随着塑胶行业的飞速发展pbt的优点是它的刚性不受温度的影响且因成型过程中通过气压传输模腔PC/PBT 基础创新塑料(美国)1731-WH9G1452.PC的优点是室温刚而韧，但高温的情况下，热变形严重。缺点是应力开裂，粘度大；3.PBT的优点是它的刚性不受温度的影响，变形小；这样共混后的材料PC-PBT即保留了两者的优点。4.PC/PBT具有较高的表面硬度，较高的刚性和韧性，也有较高的抗高温形的能力，也有较高的抗应力开裂能力；它的机械性能介于两者之间，抗高温变形对于大形的外壳类材料具有重要的意义PC/PBT 基础创新塑料(美国)1731-WH9G145。PC，PBT，PC/PBT三者的关系以及区别：1.PC/PBT是PC与PBT的共混材料，通常以共混造料后，以粒料形状供应。如果只把两种料简单的混合后，直接注塑，效果很差，会出现分层现象。2.PC的优点是室温刚而韧，但高温的情况下，热变形严重。缺点是应力开裂，粘度大；3.PBT的优点是它的刚性不受温度的影响，变形小；这样共混后的材料PC-PBT即保留了两者的优点PC/PBT 基础创新塑料(美国)1731-WH9G145。4.PC/PBT具有较高的表面硬度，较高的刚性和韧性，也有较高的抗高温形的能力，也有较高的抗应力开裂能力；它的机械性能介于两者之间，抗高温变形对于大形的外壳类材料具有重要的意义。PC/PBT 基础创新塑料(美国)1731-WH9G145用途：1.电子电器：无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳；2.汽车领域：车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖；3.工业零件：OA风扇、键盘、钓具卷线器、零件、灯罩。