SABIC Innovative Plastics Valox? V3900WX-BK1066 PBT+PC
Polymer,Thermoplastic,Polycarbonate (PC),Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced,Polyester, TP,Polybutylene Terephthalate (PBT)
SABIC Innovative Plastics (GE Plastics)
产品说明:
PBT/PC blend - Unreinforced - Flame Retardant. This is a UV-stabilized grade designed for outdoor enclosure applications requiring UL 746C F1 weatherability performance.
SABIC Innovative Plastics Valox? V3900WX PBT+PC 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| 密度 | 1.30 g/cc | 0.0470 lb/in3 | ISO 1183 |
| 水分吸收 | 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.10 % | 0.10 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0070 - 0.010 cm/cm
@Thickness 3.20 mm
|
0.0070 - 0.010 in/in
@Thickness 0.126 in
|
SABIC Method |
| 熔体流动速率 | 11 g/10 min
@Load 2.16 kg, Temperature 265 °C
|
11 g/10 min
@Load 4.76 lb, Temperature 509 °F
|
ASTM D1238 |
| 化合物熔体指数 | 9.0 g/10 min
@Load 2.16 kg, Temperature 265 °C
|
9.0 g/10 min
@Load 4.76 lb, Temperature 509 °F
|
MVR [cm^3/10 min]; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527 |
| 43.0 MPa | 6240 psi | Type I, 50 mm/min; ASTM D638 | |
| 抗张强度(屈服) | 48.0 MPa | 6960 psi | SABIC - Japan Method |
| 51.0 MPa | 7400 psi | 50 mm/min; ISO 527 | |
| 53.0 MPa | 7690 psi | Type I, 50 mm/min; ASTM D638 | |
| 伸长率 (断裂) | 42 % | 42 % | 50 mm/min; ISO 527 |
| 50 % | 50 % | Type I, 50 mm/min; ASTM D638 | |
| 250 % | 250 % | SABIC - Japan Method | |
| 屈服伸长率 | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 | |
| 拉伸模量 | 2.09 GPa | 303 ksi | 1 mm/min; ISO 527 |
| 2.20 GPa | 319 ksi | 5 mm/min; ASTM D638 | |
| 弯曲强度 | 73.0 MPa | 10600 psi | 2 mm/min; ISO 178 |
| 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | 2.13 GPa | 309 ksi | 2 mm/min; ISO 178 |
| 2.20 GPa | 319 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 悬壁梁缺口冲击强度 | 8.00 J/cm | 15.0 ft-lb/in | ASTM D256 |
| 1.10 J/cm
@Temperature -30.0 °C
|
2.06 ft-lb/in
@Temperature -22.0 °F
|
ASTM D256 | |
| 41.0 kJ/m2 | 19.5 ft-lb/in2 | 80*10*4; ISO 180/1A | |
| 8.00 kJ/m2
@Temperature -30.0 °C
|
3.81 ft-lb/in2
@Temperature -22.0 °F
|
80*10*4; ISO 180/1A | |
| 简支梁缺口冲击强度 | 5.20 J/cm2 | 24.7 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 50.0 J
@Temperature 23.0 °C
|
36.9 ft-lb
@Temperature 73.4 °F
|
ASTM D3763 |
| 50.0 J
@Temperature -40.0 °C
|
36.9 ft-lb
@Temperature -40.0 °F
|
ASTM D3763 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 表面电阻 | 6.02e+16 ohm | 6.02e+16 ohm | ASTM D257 |
| 耗散因数 | 0.0199
@Frequency 1.00e+6 Hz
|
0.0199
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 88.4 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
49.1 μin/in-°F
@Temperature -40.0 - 104 °F
|
ASTM E 831 |
| 88.4 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
49.1 μin/in-°F
@Temperature -40.0 - 104 °F
|
ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | 89.7 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
49.8 μin/in-°F
@Temperature -40.0 - 104 °F
|
ASTM E 831 |
| 89.7 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
49.8 μin/in-°F
@Temperature -40.0 - 104 °F
|
ISO 11359-2 | |
| 载荷下热变形温度(0.46 MPa) | 119 °C
@Thickness 6.40 mm
|
246 °F
@Thickness 0.252 in
|
unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 77.0 °C | 171 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 75.0 °C
@Thickness 3.20 mm
|
167 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 | |
| 96.0 °C
@Thickness 6.40 mm
|
205 °F
@Thickness 0.252 in
|
unannealed; ASTM D648 | |
| 维卡软化温度 | 105 °C | 221 °F | Rate B/50; ASTM D1525 |
| 121 °C | 250 °F | Rate B/50; ISO 306 | |
| 123 °C | 253 °F | Rate B/120; ISO 306 | |
| UL RTI | 120 °C | 248 °F | UL 746B |
| UL RTI，机械冲击 | 120 °C | 248 °F | UL 746B |
| UL RTI，机械无冲击 | 120 °C | 248 °F | UL 746B |
| 可燃性(UL94) | V-0
@Thickness 1.50 mm
|
V-0
@Thickness 0.0591 in
|
UL 94 |
| 5VA
@Thickness 3.00 mm
|
5VA
@Thickness 0.118 in
|
UL 94 | |
| 灼热丝试验 | 725 °C | 1340 °F | IEC 60695-2-13 |
| 825 °C | 1520 °F | IEC 60695-2-13 | |
| 960 °C
@Thickness 1.00 mm
|
1760 °F
@Thickness 0.0394 in
|
IEC 60695-2-12 | |
| 960 °C
@Thickness 3.00 mm
|
1760 °F
@Thickness 0.118 in
|
IEC 60695-2-12 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Ball Pressure Test, 125?°C +/- 2?°C | PASSES | IEC 60695-10-2 |
| UV-light, water exposure/immersion | F1 |
PC/PBT V3900WX 基础创新塑料 阻燃级
PC-PBT具有较高的表面硬度，较高的刚性和韧性，也有较高的抗高温形的能力，也有较高的抗应力开裂能力；它的机械性能介于两者之间
主要特点是：
高韧性，即使在低温下亦是如此
良好的耐化学性
良好的涂覆性能
良好的流动性
低吸水性
提供极低线性热膨胀系数（CLTE）品级
环保型阻燃品级
PC-PBT是PC与PBT的共混材料，通常以共混造料后，以粒料形状供应
PC-PBT是PC与PBT的共混材料，通常以共混造料后，以粒料形状供应。如果只把两种料简单的混合后，直接注塑，效果很差，会出现分层现象
PC的优点是室温刚而韧，但高温的情况下，热变形严重。缺点是应力开裂，粘度大；PBT的优点是它的刚性不受温度的影响，变形小；这样共混后的材料PC-PBT即保留了两者的优点
PC-PBT具有较高的表面硬度，较高的刚性和韧性，也有较高的抗高温形的能力，也有较高的抗应力开裂能力；它的机械性能介于两者之间
抗高温变形对于大形的外壳类材料具有重要的意义。
PC+PBT是塑料合金,它保持了结晶材料PBT的耐化学性及易于成型等特点，又兼备了非结晶材料PC的韧性和尺寸稳定性。其产品广泛应用于汽车保险杠、汽车拉手、电子元件等。 PC/PBT具有PC和PBT二者的综合特性，例如PC的高韧性和几何稳定性以及PBT的化学稳定性、热稳定性和润滑特性等。
PC+PBT是塑料合金,它保持了结晶材料PBT的耐化学性及易于成型等特点，又兼备了非结晶材料PC的韧性和尺寸稳定性。其产品广泛应用于汽车保险杠、汽车拉手、电子元件等。 PC/PBT具有PC和PBT二者的综合特性，例如PC的高韧性和几何稳定性以及PBT的化学稳定性、热稳定性和润滑特性等。
典型应用范围:齿轮箱、汽车保险杠以及要求具有抗化学反应和耐腐蚀性、热稳定性、抗冲击性以及几何稳定性的产品。
注塑模工艺条件:干燥处理：建议110~135C,约4小时的干燥处理。
熔化温度：235~300C。 模具温度：37~93C。
化学和物理特性C/PBT具有PC和PBT二者的综合特性，例如PC的高韧性和几何稳定性以及PBT的化学稳定性、热稳定性和润滑特性等。