东莞市宏阔塑胶有限公司
SABIC Innovative Plastics LNP Thermocomp HX05073
聚酰胺12
Polymer,Thermoplastic,Nylon,Nylon 12
SABIC Innovative Plastics (GE Plastics)
产品说明:
LNP THERMOCOMP* HX05073 is a compound based on Nylon 12 resin containing Glass Fiber.
This data was supplied by SABIC-IP for the Americas region.
SABIC Innovative Plastics LNP Thermocomp HX05073 PA 12 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.26 g/cc | 0.0455 lb/in3 | ISO 1183 |
| 1.263 g/cc | 0.04563 lb/in3 | ASTM D 792 | |
| 平衡吸湿 | 0.15 %
@Time 86400 sec
|
0.15 %
@Time 24.0 hour
|
50% RH; ASTM D 570 |
| 线性模具收缩，Flow | 0.0011 cm/cm
@Time 86400 sec
|
0.0011 in/in
@Time 24.0 hour
|
ISO 294 |
| 0.0010 - 0.0020 cm/cm
@Time 86400 sec
|
0.0010 - 0.0020 in/in
@Time 24.0 hour
|
ASTM D 955 | |
| 线性成型收缩率,横向 | 0.0062 cm/cm
@Time 86400 sec
|
0.0062 in/in
@Time 24.0 hour
|
ISO 294 |
| 0.0060 - 0.0070 cm/cm
@Time 86400 sec
|
0.0060 - 0.0070 in/in
@Time 24.0 hour
|
ASTM D 955 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 130 MPa | 18900 psi | ISO 527 |
| 134 MPa | 19400 psi | ASTM D 638 | |
| 伸长率 (断裂) | 6.2 % | 6.2 % | ASTM D 638 |
| 6.3 % | 6.3 % | ISO 527 | |
| 拉伸模量 | 7.08 GPa | 1030 ksi | 1 mm/min; ISO 527 |
| 7.37 GPa | 1070 ksi | 50 mm/min; ASTM D 638 | |
| 弯曲强度 | 193 MPa | 28000 psi | ISO 178 |
| 195 MPa | 28300 psi | ASTM D 790 | |
| 弯曲模量 | 6.20 GPa | 899 ksi | ASTM D 790 |
| 6.64 GPa | 963 ksi | ISO 178 | |
| 悬壁梁缺口冲击强度 | 2.56 J/cm
@Temperature 23.0 °C
|
4.80 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 256 |
| 悬壁梁无缺口冲击强度 | 14.31 J/cm
@Temperature 23.0 °C
|
26.81 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 4812 |
| 悬壁梁缺口冲击强度 | 25.0 kJ/m2
@Temperature 23.0 °C
|
11.9 ft-lb/in2
@Temperature 73.4 °F
|
80*10*4; ISO 180/1A |
| 悬壁梁无缺口冲击强度 | 87.0 kJ/m2
@Temperature 23.0 °C
|
41.4 ft-lb/in2
@Temperature 73.4 °F
|
80*10*4; ISO 180/1U |
| 冲击试验 | 6.00 J | 4.43 ft-lb | Multiaxial Impact; ISO 6603 |
| 16.0 J
@Temperature 23.0 °C
|
11.8 ft-lb
@Temperature 73.4 °F
|
Instrumented Impact Energy @ peak; ASTM D 3763 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 34.3 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
19.1 μin/in-°F
@Temperature -40.0 - 104 °F
|
ASTM E 831 |
| 34.4 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
19.1 μin/in-°F
@Temperature -40.0 - 104 °F
|
ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | 99.7 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
55.4 μin/in-°F
@Temperature -40.0 - 104 °F
|
ASTM E 831 |
| 99.7 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
55.4 μin/in-°F
@Temperature -40.0 - 104 °F
|
ISO 11359-2 | |
| 载荷下热变形温度(1.8 MPa) | 174 °C | 345 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 178 °C
@Thickness 3.20 mm
|
352 °F
@Thickness 0.126 in
|
unannealed; ASTM D 648 |
PA12用途 :
尼龙主要用于汽车工业,电气电子工业,交通运输业,机械制造工业,电线电缆通讯业,薄膜及日常用品.制造各种轴承,齿轮,圆齿轮、凸轮、伞齿轮、输油管,储油器,保护罩,支撑架,车轮罩盖,导流板,风扇,空气过滤器外壳,散热器水室,制动管,发动机罩,车门把手.轴承、齿轮、滑轮泵叶轮、叶片、高压密封圈、垫、阀座、衬套、输油管、贮油器、绳索、传动带、砂轮胶粘剂、电池箱、电器线圈、电缆接头各种滚子、滑轮、泵叶轮、风扇叶片、蜗轮、推进器、螺钉、螺母、耐油密封垫片、耐油容器、外壳、软管、电缆护套、剪切机、滑轮套、牛头刨床滑块 电磁分配阀座、冷陈设备、衬垫、轴承保持架、汽车和拖拉机上各种输油管、活塞、绳索、传动皮带，纺织机械工业设备零雾料，以及日用品和包装薄膜等。等。还有包装用带、食品用薄膜（熟食用的高温薄膜和清凉饮料用的低温薄膜）的产量也相当大。
PA12性能：
PA12对强氧化性酸无抵抗能力。PA12的粘性主要取决于湿度、温度和储藏时间。它的流动性很好。收缩率在0.5%到2%之间，这主要取决于材料品种、壁厚及其它工艺条件PA12 聚酰胺12或尼龙12典型应用范围:水量表和其他商业设备，电缆套，机械凸轮，滑动机构及轴承等.PA12是从丁二烯线性，半结晶-结晶热塑性材料。
工艺条件
干燥处理：加工之前应保证含水率在0.1%以下。如果材料是暴露在空气中储存，建议要在80C除湿干燥4~8小时。如果材料是在密闭容器中储存，那么经过3小时温度平衡即可直接使用。
熔融温度：240~300℃；对于普通特性材料不要超过310℃，对于有阻燃特性材料不要超过270℃。
高速注射速度可使成型良好。
PA12尼龙12弹性体有优良的噪音和振动阻尼性，在干燥运转条件下，对钢、POM、PBT和其他材料的滑动摩擦系数低、优良的损性和高体积稳定性。正因为这些性质，该产品特别适用于DVD、CD、MD、VCR、便携式摄像机、数码相机、打印机和录像机等的无声齿轮。
PA12料筒温度：
进料段：230—240℃
中段：255—265℃
出料段：265—275℃
喷嘴：295—300℃
模温：60－80℃
注射压力：80—110mpa
成型周期：20—25秒
螺杆转速：30—60 r/min
说明：
1.若充模不满：提高炮筒温度10—15℃，也不要提高注塑压力和速度，以免产生水花；
2.若塑件发白起雾：请提高料筒温度10－15℃，压力70－100mpa，速度中速，使排气良好；
3.若粘模或者变黄色：请降低炮筒温度10—15℃，降低注塑压力和速度；
4.烁斑的解决：