PPS FORTRON ICE 506L

Physical Properties	Metric	English	Comments
Specific Gravity	1.60g/cc	1.60g/cc	ASTM D792
Density	1.65g/cc	0.0596lb/in3	ISO 1183
Water Absorption	0.020 % @Temperature 22.8 °C	0.020 % @Temperature 73.0 °F	24hr immersion; ASTM D570
Water Absorption at Saturation	0.020 %	0.020 %	ISO 62
Linear Mold Shrinkage, Flow	0.0020-0.0030cm/cm	0.0020-0.0030in/in	ASTM D955
	0.0020-0.0060cm/cm	0.0020-0.0060in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.0040-0.0060cm/cm	0.0040-0.0060in/in	ISO 294-4
	0.0050-0.0070cm/cm	0.0050-0.0070in/in	ASTM D955
Melt Flow	19g/10 min	19g/10 min	ASTM D1238
Spiral Flow	21.5cm	8.46in
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	100	100	ISO 2039-2
	100	100	ASTM D785
Tensile Strength at Break	195MPa	28300psi	5mm/min; ISO 527-2/1A
	200MPa	29000psi	ASTM D638
Elongation at Break	1.9 %	1.9 %	5mm/min; ISO 527-2/1A
	2.0 %	2.0 %	ASTM D638
Tensile Modulus	14.7GPa	2130ksi	50mm/min; ISO 527-2/1A
Flexural Strength	276MPa	40000psi	ASTM D790
	285MPa	41300psi	ISO 178

PPS FORTRON ICE 506L

性能

1、电绝缘性(尤其高频绝缘性)优良,白色硬而脆?跌落于地上有金属响声,透光率仅次于有机玻璃,着色性耐水性,化学稳定性良好 。有优良的阻燃性?为不燃塑料。 2、强度一般?刚性很好,但质脆,易产生应力脆裂,不耐苯.汽油等有机溶剂.长期使用温度可达260度 ?在400度的空气或氮气中保持稳定。通过加玻璃纤维或其它增强材料改性后?可以使冲击强度大为提高?耐热性和其它机械性能也有所提高?密度增加到1.6-1.9?成型收缩率较小到0.15-0.25% 适于制作耐热件.绝缘件及化学仪器.光学仪器等零件。 成型性能 1.无定形料,吸湿小,但宜干燥后成型。 2.流动性介于ABS和PC之间?凝固快?收缩小?易分解?选用较高的注射压力和注射速度。模温取100-150度。主流道锥度应大?流道应短。 应用范围 一般可应用于制造PPS管、PPS板材等材料?多用于建筑、家居方面

1、机械工业：机械工业中特别运用于在高湿、强腐蚀的环境下的部件制备。用于壳体、结构件、耐磨件及密封材料，具体有如：泵壳、泵轮、阀、轴承、轴承支架、活塞环及齿轮、滑轮、风扇、流量计部件、法兰盘、万向头、计数器、水准仪等。

2、电子电器：微型电子元件封装、连接器、接线器、插座、线圈骨架、马达壳、电磁调节盘、电视高频头轴、继电器、微调电容器、保险丝支架、收录机、磁疗器等零部件。还应用于精密仪器：电脑、计时器、转速器、复印机、照相机、温度传感器以及各种测量仪表的壳体和部件。

3、汽车工业：PPS用于汽车工业占45%左右，主要用于汽车功能件；点火器、加热器、汽化器、离合器、变速器、齿轮箱、轴承支架、灯罩、保险杠、风扇、排气系统以及反光镜和车灯座的零部件。可代替金属制作排气筒循环阀及水泵叶轮，气动信号调解器等。

4、家用电器：热风筒、卷发器、干发器、烫发器、微波炉、咖啡煲、干衣机、电熨斗、电饭煲等的防护涂层和零部件。

5、化学工业：PPS具有优良粘接性和耐蚀性，极宜作化工设备的衬里。

PPS FORTRON ICE 506L 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！