东莞市天之鸿塑化有限公司
低密度/TPV 荷兰DSM 6135N
Sarlink? TPV X6100 系列是专为需要卓越着色性和弹性性能的消费、汽车和工业应用而设计的工程材料。Sarlink? TPV 6135N 是一种低硬度、低密度、多用途的热塑性硫化橡胶,无需预干燥,可通过注塑成型加工。
特性
|
|
|||
用途
|
|
|||
RoHS 合规性
|
|
|||
外观
|
|
|||
形式
|
|
|||
加工方法
|
|
物理性能 |
额定值
|
单位制
|
测试方法
|
密度 / 比重
|
|||
--
|
0.886
|
g/cm3
|
ASTM D792 |
--
|
0.888
|
g/cm3
|
ISO 1183 |
硬度 |
额定值
|
单位制
|
测试方法
|
肖氏硬度
|
ASTM D2240,ISO 868 | ||
邵氏 A, 5 秒, 挤塑
|
32
|
||
邵氏 A, 5 秒, 注塑
|
36
|
弹性体 |
额定值
|
单位制
|
测试方法
|
拉伸应力
|
ASTM D412,ISO 37 | ||
横向流量 : 100%应变
|
0.800
|
MPa
|
|
流量 : 100%应变
|
1.10
|
MPa
|
|
抗张强度
|
ASTM D412,ISO 37 | ||
横向流量 : 断裂
|
2.70
|
MPa
|
|
流量 : 断裂
|
2.30
|
MPa
|
|
伸长率
|
ASTM D412,ISO 37 | ||
横向流量 : 断裂
|
560
|
%
|
|
流量 : 断裂
|
370
|
%
|
|
撕裂强度
|
|||
横向流量
|
10.5
|
kN/m
|
ASTM D624 |
--2
|
10.5
|
kN/m
|
ISO 34-1 |
压缩永久变形
|
ASTM D395,ISO 815 | ||
23°C, 22 hr
|
23
|
%
|
|
70°C, 22 hr
|
30
|
%
|
|
125°C, 70 hr
|
43
|
%
|
补充信息 |
额定值
|
单位制
|
测试方法
|
Apparent Shear Viscosity - Capillary @ 206/s
|
|||
200°C
|
195
|
Pa·s
|
ASTM D3835 |
200°C
|
195
|
Pa·s
|
ISO 11443 |
法律声明 | |||
The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.
|
注射 |
额定值
|
单位制
|
|
料筒后部温度
|
138 到 160
|
°C
|
|
料筒中部温度
|
166 到 193
|
°C
|
|
料筒前部温度
|
177 到 227
|
°C
|
|
射嘴温度
|
182 到 227
|
°C
|
|
加工(熔体)温度
|
182 到 227
|
°C
|
|
模具温度
|
16 到 54
|
°C
|
|
注射速度
|
快速
|
||
背压
|
0.345 到 1.03
|
MPa
|
|
螺杆转速
|
25 到 75
|
rpm
|