东莞市宏阔塑胶有限公司
KRATON? D1161 J
苯乙烯-异戊二烯-苯乙烯嵌段共聚物
Kraton Polymers LLC
产品说明：
Kraton D1161 J Polymer is a clear, linear block copolymer based on styrene and isoprene with bound styrene of 15% mass. It is supplied from Japan in the physical form(s) identified in the grade nomenclature below.
Kraton D1161 J Polymer is used in formulating adhesives, sealants and coatings. It is also used as a modifier of bitumen and polymers and in formulating compounds.
- D1161 JSP - supplied as dusted dense pellets
- D1161 JS - supplied as dusted crumb
- D1161 JU - supplied as undusted crumb
Kraton D1161 J Polymer is used in formulating adhesives, sealants and coatings. It is also used as a modifier of bitumen and polymers and in formulating compounds.
KRATON? D1161 J 物性表
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 外观 |
|
| 形式 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.920 | g/cm3 | |
| 熔流率（熔体流动速率）(190°C/2.16 kg) | 1.3 到 3.7 | g/10 min | ISO 1133 |
| 结合苯乙烯 | 15.0 | % | |
| 灰份含量 | ISO 247 | ||
| JS | % | ISO 247 | |
| JSP | % | ISO 247 | |
| JU | % | ISO 247 | |
| 挥发物 - 2hr (110°C) | % | 内部方法 | |
| 溶液粘度 - Toluene, 25%wt (25°C) | 0.90 到 1.7 | Pa·s | 内部方法 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度(邵氏 A, 30 秒) | 37 | ISO 7619 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力(300%应变) | 0.900 | MPa | ISO 37 |
| 拉伸应力(屈服) | 28.0 | MPa | ISO 37 |
| 伸长率(断裂) | 1300 | % | ISO 37 |
SIS日本科腾D1161JSP-苯乙烯一异戊二烯一苯乙烯，它具有的波纹密封性和高温保持力，其独特的微观分相结构决定了它在用做粘合剂时具有独特的性，配制成的压敏胶和热熔胶广泛应用于医疗、电绝缘、包装、保护掩蔽、标志、粘接固定等领域，特别是其生产热熔压敏胶(HMPSA)，具有不含溶剂、、能耗小、设备简单、粘接范围广的特点，深受用户欢迎，近年来的发展速度很快。
SIS是一种热塑性弹性体，为苯乙烯和异戊二烯的嵌段共聚物，兼具橡胶和塑料的性质，尤其在做粘接材料时性能优异。
①具有流变性能，溶液粘度只有SBS的2/3，流动性好，为提高生产效率提供了条件。
②SIS与其他材料的相容性优于SBS，加工原辅材料容易选取。
③在抗老化性能上，SBS类粘合剂在使用6个月或更长时间后，初粘力丧失殆尽，而SIS变化不大。
④在热熔胶应用上，SBS渗油现象较严重，较快失去粘接性能，而SIS无此现象，产品质量档次高，保质期长。
SIS的用途：用作热熔压敏胶粘剂、涂料、溶剂型粘合剂、塑料改性制品、嵌缝材料等方面的主体材料，用于热熔压敏胶时，其下游产品如包装带、妇女卫生巾、双面胶带及耐油标签等性能更佳。