尼龙 9T/GN2332/Kuraray Co., Ltd. 物性表
尼龙 9T/GN2332/Kuraray Co., Ltd.
规格用途
| 规格级别 | |
| 外观颜色 | |
| 该料用途 | 薄壁部件; 电气/电子应用领域 |
| 备注说明 | GN2332 improves flow-ability in thin-walled parts. For components requiring high flow-ability, such as 0.3 mm pitch connectors, this high-flow grade is used. |
技术参数
| 性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 | |
| 物理性能 | 密度 / 比重 | 1.62 | g/cm3 | ||
| 熔流率（熔体流动速率） | ASTM D1238 | ||||
| 320°C/2.16 kg | 60 | g/10 min | |||
| 收缩率 | |||||
| 流动 : 1.00 mm | 0.10 | % | |||
| 横向流动 : 1.00 mm | 0.60 | % | |||
| 吸水率 | |||||
| 平衡, 40°C, 95%RH | 1.0 | % | |||
| 热性能 | 载荷下热变形温度 | ASTM D648 | |||
| 1.8 MPa, 未退火 | 285 | °C | |||
| 玻璃转化温度 | 125 | °C | |||
| 熔融温度 | 306 | °C | |||
| 可燃性 | UL 阻燃等级 | UL 94 | V-0 | ||
| Bar Flow Length | |||||
| 320°C, 500.0 μm | 8.50 | cm | |||
| Weld Elongation | ASTM D638 | 0.30 | % | ||
| Weld Strength | ASTM D638 | 36.0 | MPa | ||
| 电气性能 | 体积电阻率 | ASTM D257 | 1.0E+16 | ohms·cm | |
| 介电强度 | ASTM D149 | 30 | kV/mm | ||
| 介电常数 | ASTM D150 | ||||
| 10.0 GHz | 3.40 | ||||
| 耗散因数 | ASTM D150 | ||||
| 10.0 GHz | 0.010 | ||||
| 相比耐漏电起痕指数(CTI) | UL 746 | PLC 1 | |||
| 机械性能 | 抗张强度 | ASTM D638 | 165 | MPa | |
| 伸长率 | ASTM D638 | ||||
| 断裂 | 3.8 | % | |||
| 弯曲模量 | ASTM D790 | 11000 | MPa | ||
| 弯曲强度 | ASTM D790 | 215 | MPa | ||
| 冲击性能 | 悬壁梁缺口冲击强度 | ASTM D256 | 110 | J/m |