COC TOPAS 5013L-10 产品说明：

Product Description
TOPAS 5013L-10 is a high flow, internally lubricated injection molding grade with a 130°C heat distortion temperature. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for healthcare and other high-tech products. The 5013 resin series features high flow characteristics for excellent mold detail replication. This grade has a high heat distortion temperature to withstand 95°C PCR protocols, is suitable for gamma or EtO procedures.

物理性能	额定值	单位制	测试方法
密度	1.02	g/cm3	ISO 1183
熔流率（熔体流动速率）(260°C/2.16 kg)	44	g/10 min	ISO 1133
溶化体积流率（MVR）(260°C/2.16 kg)	48.0	cm3/10min	ISO 1133
收缩率1	0.10 到 0.30	%	内部方法
吸水率(饱和, 23°C)	0.010	%	ISO 62

机械性能	额定值	单位制	测试方法
拉伸模量	3200	MPa	ISO 527-2/1A/1
拉伸应力(屈服)	46.0	MPa	ISO 527-2/1A/50
拉伸应变(屈服)	1.7	%	ISO 527-2/1A/50

冲击性能	额定值	单位制	测试方法
简支梁缺口冲击强度(23°C)	1.6	kJ/m2	ISO 179/1eA
简支梁无缺口冲击强度(23°C)	13	kJ/m2	ISO 179/1eU

热性能	额定值	单位制	测试方法
热变形温度(0.45 MPa, 未退火)	127	°C	ISO 75-2/B
玻璃转化温度	134	°C	ISO 11357-2

COC TOPAS 5013L-10

药物输送精密，部件预充式注射器，西林瓶，子弹瓶和管手术器械四，容器和组件您高温光学电子食品包装医疗保健和食品接触

领导属性

低溶出物和萃取物，低水传输尺寸稳定性，高公差非离子型，不提倡像玻璃吸附微反应醇，丙酮，和丙烯酸酯的化学耐受性透明，可承受ETO /伽玛/蒸汽灭菌耐温性，清晰度和纯度净度，低双折射，潮湿敏感度低;低介电常数，热塑性不制造双酚A，邻苯二甲酸盐或卤素广泛的合规性

相关牌号为注塑，医疗，光学和诊断

TOPAS 6013M-07 - 更广泛的加工窗口，最好的吹塑（IBM / ISBM）TOPAS 6015S-04 - 高耐热变形性（150℃）为134°C的协议TOPAS IT的应用需要额外的韧性X1 - 冲级。

COC特性：

环烯烃共聚物 是一种无定形高分子聚合物制造商生产的几个。 COC是一类新的聚合物相对较 聚丙烯 和 聚乙烯。这种材料主要用于要求玻璃般清晰包括镜头，瓶，显示器和医疗

设备的应用程序。COCs良好的耐化学性。

挤压 COC既可以挤压铸造和吹膜设备。主要用于消费应用，包括食品和药品包装。

成型 COC是主要用于注射成型。

TOPAS是宝理公司开发出来的环烯烃类共聚物（COC）的商品名，是具有环状烯烃结构的非晶性透明共聚高分子。

TOPAS 具有与PMMA（聚甲基丙烯酸甲酯、丙烯酸树脂）相匹敌的光学性能以及具有高于PC（聚碳酸酯）的耐热性，还具有比PMMA和PC更加优良的尺寸稳定性等，在市场上获得了很

高的评价。再有，TOPAS 还具有改善水蒸汽气密性，增加刚性、耐热性，易赋予切割性能等优点，作为适合于用作传统材料的改性用材料，它在包装材料领域里的开发活动正在推进之中。是玻璃材料的最佳替代材料。