东莞市常平浩云塑胶经营部
RTP Compounds 2800 B-30D FR TPV
RTP Compounds 2800 B-30D HF TPV
RTP Compounds 2800 B-40A FR TPV
RTP Compounds 2800 B-40D FR TPV
RTP Compounds 2800 B-40D FR TPV
RTP Compounds 2800 B-45A FR TPV
RTP Compounds 2800 B-45A HF TPV
RTP Compounds 2800 B-45A Z TPV
RTP Compounds 2800 B-45A TPV
RTP Compounds 2800 B-50A FR TPV
RTP Compounds 2800 B-50D FR TPV
RTP Compounds 2800 B-55A FR TPV
RTP Compounds 2800 B-55A UV TPV
RTP Compounds 2800 B-55A Z TPV
RTP Compounds 2800 B-55A TPV
RTP Compounds 2800 B-60A FR TPV
RTP Compounds 2800 B-65A TPV
RTP Compounds 2800 B-65D TPV
RTP Compounds 2800 B-70A Z TPV
RTP Compounds 2800 B-75A FR TPV
RTP Compounds 2800 B-75A HB TPV
RTP Compounds 2800 B-75A HF TPV
RTP Compounds 2800 B-75A Z TPV
RTP Compounds 2800 B-75A TPV
RTP Compounds 2800 B-75D TPV
RTP Compounds 2800 B-85A HF TPV
RTP Compounds 2800 B-85A Z TPV
RTP Compounds 2800 B-85A TPV
RTP Compounds 2800B-30D TPV
RTP Compounds 2800B-40A HF TPV
RTP Compounds 2800B-40A TPV
RTP Compounds 2800B-40D HF TPV
RTP Compounds 2800B-45A HF UV TPV
RTP Compounds 2800B-50A HF TPV
RTP Compounds 2800B-50A TPV
RTP Compounds 2800B-50D HF TPV
RTP Compounds 2800B-50D TPV
RTP Compounds 2800B-55A HF UV TPV
RTP Compounds 2800B-55A HF TPV
RTP Compounds 2800B-60A HF TPV
RTP Compounds 2800B-60A TPV
RTP Compounds 2800B-60D FR TPV
RTP Compounds 2800B-70A FR TPV
RTP Compounds 2800B-70A HF TPV
RTP Compounds 2800B-70A TPV
RTP Compounds 2800B-80A FR TPV
RTP Compounds 2800B-80A HF TPV
RTP Compounds 2800B-80A TPV
RTP Compounds 2800B-90A TPV
RTP Compounds ESD C 2800 B-55A Black TPV
RTP Compounds ESD C 2800 B-85A Black TPV
RTP 2800 B-85A
热塑性硫化橡胶
RTP Company
产品说明：
Warning: The status of this material is 'Commercial: Limited Issue'
The data for this material has not been recently verified.
The data for this material has not been recently verified.
Please contact RTP Company for current information prior to specifying this grade.
RTP 2800 B-85A 物性表
| 基本信息 | |
|---|---|
| RoHS 合规性 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.02 | g/cm3 | ASTM D792 |
| 收缩率 - 流动(3.20 mm) | 1.4 到 1.7 | % | ASTM D955 |
| 含水量 | % |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度(邵氏 A, 10 秒) | 85 | ASTM D2240 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力 | ASTM D412 | ||
| 50%应变, 3.18 mm1 | 5.52 | MPa | ASTM D412 |
| 100%应变, 3.18 mm2 | 6.07 | MPa | ASTM D412 |
| 300%应变, 3.18 mm3 | 7.58 | MPa | ASTM D412 |
| 抗张强度4(屈服, 3.20 mm) | 10.3 | MPa | ASTM D412 |
| 伸长率5(断裂) | 750 | % | ASTM D412 |
| 撕裂强度6 | 49.0 | kN/m | ASTM D624 |
| 压缩永久变形7 | ASTM D395B | ||
| 23°C, 22 hr | 35 | % | ASTM D395B |
| 70°C, 22 hr | 56 | % | ASTM D395B |
| 可燃性 | 额定值 | 测试方法 | |
|---|---|---|---|
| UL 阻燃等级(1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 79.4 | °C | |
| 干燥时间 | 2.0 到 3.0 | hr | |
| Dew Point | -17.8 | °C | |
| 加工（熔体）温度 | 193 到 227 | °C | |
| 模具温度 | 10.0 到 79.4 | °C | |
| 注塑压力 | 68.9 到 103 | MPa |
| 备注 | |
|---|---|
| 1 . | C 模具, 510 mm/min |
| 2 . | 口模 C, 510 mm/min |
| 3 . | C 模具, 510 mm/min |
| 4 . | C 模具, 500 mm/min |
| 5 . | 口模 C, 500 mm/min |
| 6 . | C 模具 |
| 7 . | 类型2 |