Lupoy NS5000

Technical Datasheet |Supplied by LG Chem

Lupoy? NS5000 is a high flow polycarbonate and acrylonitrile butadiene styrene (PC/ ABS) alloy by LG Chem. Exhibits high performance, high impact resistance and medium heat resistance. Lupoy? NS5000 is suitable for processing by injection molding. Used in automotive interiors. Complies with IMDS ID 36129964.

Physical Properties	Metric	English	Comments
Specific Gravity	1.14g/cc	1.14g/cc	ASTM D792
Maximum Moisture Content	0.020	0.020	Injection Molding
Linear Mold Shrinkage, Flow	0.0050-0.0080cm/cm @Thickness 3.20 mm	0.0050-0.0080in/in @Thickness 0.126 in	ASTM D955
Melt Flow	5.5g/10 min @Load 2.16 kg, Temperature 250 °C	5.5g/10 min @Load 4.76 lb, Temperature 482 °F	ASTM D1238
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	114	114	ASTM D785
Tensile Strength, Yield	56.9MPa @Thickness 3.20 mm	8250psi @Thickness 0.126 in	50mm/min; ASTM D638
Elongation at Break	= 100 % @Thickness 3.20 mm	= 100 % @Thickness 0.126 in	50mm/min; ASTM D638
Flexural Yield Strength	86.3MPa @Thickness 3.20 mm	12500psi @Thickness 0.126 in	10mm/min; ASTM D790
Flexural Modulus	2.26GPa @Thickness 3.20 mm	327ksi @Thickness 0.126 in	10mm/min; ASTM D790

PC/ABS LUPOY NS5000

PC/ABS，聚碳酸酯和丙烯腈-丁二烯-苯乙烯共聚物和混合物，是由聚碳酸酯（Polycarbonate）和聚丙烯腈（ABS）合金而成的热可塑性塑胶，结合了两种材料的优异特性，ABS材料的成型性和PC的机械性、冲击强度和耐温、抗紫外线（UV）等性质，可广泛使用在汽车内部零件、事务机器、通信器材、家电用品及照明设备上。

性能

1、一般性能

ABS工程塑料外观为不透明呈象牙色粒料，其制品可着成五颜六色，并具有高光泽度。ABS相对密度为1.05左右，吸水率低。ABS同其他材料的结合性好，易于表面印刷、涂层和镀层处理。ABS的氧指数为18~20，属易燃聚合物，火焰呈黄色，有黑烟，并发出特殊的肉桂味。

2、力学性能

ABS有优良的力学性能，其冲击强度极好，可以在极低的温度下使用：ABS的耐磨性优良，尺寸稳定性好，又具有耐油性，可用于中等载荷和转速下的轴承。ABS的耐蠕变性比PSF及PC大，但比PA及POM小。ABS的弯曲强度和压缩强度属塑料中较差的。ABS的力学性能受温度的影响较大。

3、热学性能

ABS的热变形温度为93~118℃，制品经退火处理后还可提高10℃左右。ABS在-40℃时仍能表现出一点的韧性，可在-40~100℃的温度范围内使用。

4、电学性能

ABS的电绝缘性较好，并且几乎不受温度、湿度和频率的影响，可在大多数环境下使用。

5、环境性能

ABS不受水、无机盐、碱及多种酸的影响，但可溶于酮类、醛类及氯代烃中，受冰乙酸、植物油等侵蚀会产生应力开裂。ABS的耐候性差，在紫外光的作用下易产生降解；于户外半年后，冲击强度下降一半