Lupoy GP5100
Technical Datasheet |Supplied by LG Chem
Lupoy? GP5100 is a general purpose polycarbonate and acrylonitrile butadiene styrene (PC/ ABS) alloy by LG Chem, reinforced with 10% glass fiber. Exhibits high performance and dimensional stability. Lupoy? GP5100 is suitable for processing by injection molding. Used in electrical appliance housings and automotive instrument panels.
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.16-1.20g/cc | 1.16-1.20g/cc | ASTM D792 |
Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
Linear Mold Shrinkage, Flow | 0.0030-0.0040cm/cm
|
0.0030-0.0040in/in
|
ASTM D955 |
Melt Flow | 4.0g/10 min
|
4.0g/10 min
|
ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 88.3MPa
|
12800psi
|
5mm/min; ASTM D638 |
Elongation at Break | 6.0 %
|
6.0 %
|
5mm/min; ASTM D638 |
Flexural Yield Strength | 137MPa
|
19900psi
|
1.3mm/min; ASTM D790 |
Flexural Modulus | 4.81GPa
|
697ksi
|
1.3mm/min; ASTM D790 |
Izod Impact, Notched | =0.981J/cm
|
=1.84ft-lb/in
|
ASTM D256 |
PC/ABS LUPOY GP5100
PC/ABS,聚碳酸酯和丙烯腈-丁二烯-苯乙烯共聚物和混合物,是由聚碳酸酯(Polycarbonate)和聚丙烯腈(ABS)合金而成的热可塑性塑胶,结合了两种材料的优异特性,ABS材料的成型性和PC的机械性、冲击强度和耐温、抗紫外线(UV)等性质,可广泛使用在汽车内部零件、事务机器、通信器材、家电用品及照明设备上。
性能
1、一般性能
ABS工程塑料外观为不透明呈象牙色粒料,其制品可着成五颜六色,并具有高光泽度。ABS相对密度为1.05左右,吸水率低。ABS同其他材料的结合性好,易于表面印刷、涂层和镀层处理。ABS的氧指数为18~20,属易燃聚合物,火焰呈黄色,有黑烟,并发出特殊的肉桂味。
2、力学性能
ABS有优良的力学性能,其冲击强度极好,可以在极低的温度下使用:ABS的耐磨性优良,尺寸稳定性好,又具有耐油性,可用于中等载荷和转速下的轴承。ABS的耐蠕变性比PSF及PC大,但比PA及POM小。ABS的弯曲强度和压缩强度属塑料中较差的。ABS的力学性能受温度的影响较大。
3、热学性能
ABS的热变形温度为93~118℃,制品经退火处理后还可提高10℃左右。ABS在-40℃时仍能表现出一点的韧性,可在-40~100℃的温度范围内使用。
4、电学性能
ABS的电绝缘性较好,并且几乎不受温度、湿度和频率的影响,可在大多数环境下使用。
5、环境性能
ABS不受水、无机盐、碱及多种酸的影响,但可溶于酮类、醛类及氯代烃中,受冰乙酸、植物油等侵蚀会产生应力开裂。ABS的耐候性差,在紫外光的作用下易产生降解;于户外半年后,冲击强度下降一半