东莞市铭汇塑胶有限公司
Lupolen 2426 K
低密度聚乙烯
LyondellBasell Industries
产品说明:
Lupolen 2426 K is an additivated, low density polyethylene. It contains slip and anti-blocking agent. It is delivered in pellet form.
Foodlaw compliance information about this product can be found in separate product documentation.
This product is not intended for use in medical and pharmaceutical applications.
Foodlaw compliance information about this product can be found in separate product documentation.
This product is not intended for use in medical and pharmaceutical applications.
![2.jpg 2.jpg](https://img1.51pla.com/51pla/images/202204/24/33262c87b113a8f704dfd4202522c3c5.jpg)
基本信息 | |
---|---|
添加剂 |
|
特性 |
|
用途 |
|
形式 |
|
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
密度 | 0.924 | g/cm3 | ISO 1183 |
熔流率(熔体流动速率)(190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸模量 | 260 | MPa | ISO 527-2 |
拉伸应力(屈服) | 11.0 | MPa | ISO 527-2 |
摩擦系数 | 0.20 | ISO 8295 |
薄膜 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
薄膜厚度 - 经测试 | 50 | μm | |
可供应的薄膜厚度 | 0.6-1.6 mil (15-40 μ) | ||
抗张强度 | ISO 527-3 | ||
MD : 50 μm, 吹塑薄膜 | 19.0 | MPa | ISO 527-3 |
TD : 50 μm, 吹塑薄膜 | 16.0 | MPa | ISO 527-3 |
伸长率 | ISO 527-3 | ||
MD : 断裂, 50 μm, 吹塑薄膜 | 300 | % | ISO 527-3 |
TD : 断裂, 50 μm, 吹塑薄膜 | 600 | % | ISO 527-3 |
落锤冲击(50 μm, 吹塑薄膜) | 100 | g | ASTM D1709 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
维卡软化温度 | 92.0 | °C | ISO 306/A50 |
溶融温度(DSC) | 111 | °C | ISO 3146 |
光学性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
光泽度 | ASTM D2457 | ||
20°, 50.0 μm, 吹塑薄膜 | 50 | ASTM D2457 | |
60°, 50.0 μm, 吹塑薄膜 | 100 | ASTM D2457 | |
雾度(50.0 μm, 吹塑薄膜) | 9.0 | % | ASTM D1003 |
补充信息 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
Failure Energy(50.0 μm) | 35.0 | J/cm | DIN 53373 |
Film properties tested using 50 μm thickness blown film extruded at a melt temperature of 170°C and a blow-up ratio of 1:2.5. |
挤出 | 额定值 | 单位制 | |
---|---|---|---|
熔体温度 | 150 到 190 | °C |