江苏普及塑料有限公司
| 牌号简介About |
|---|
| 35%玻璃纤维增强，ppa，为电气和电子应用开发的高性能聚酰胺 35% Glass Reinforced, PPA, High Performance Polyamide Developed for Electrical and Electronics Applications |
产品描述Product Description
厂家：美国杜邦DuPont Canada, Inc. - Dartek Division
类别：PPAPPA
用途：电气/电子应用领域;
加工条件：注射成型Injection Molding
性能特点：热稳定性好;Heat Stabilized
填料：玻璃纤维 35
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Density | 1.47 | g/cm3 | ISO 1183 |
| 收缩率Molding Shrinkage | ISO 294-4 | ||
| TDAcross Flow | 0.60 | % | ISO 294-4 |
| MDFlow | 0.20 | % | ISO 294-4 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量Tensile Modulus | 12100 | MPa | ISO 527-2 |
| 拉伸强度拉伸强度 | |||
| 断裂断裂 | 220 | MPa | ISO 527-2 |
| 拉伸应变拉伸应变 | |||
| 断裂断裂 | 2.4 | % | ISO 527-2 |
| 弯曲模量Flexural Modulus | 11000 | MPa | ISO 178 |
| 弯曲强度Flexural Stress | 300 | MPa | ISO 178 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度简支梁缺口冲击强度 | |||
| 23℃23℃ | 10 | kJ/m2 | ISO 179/1eA |
| 简支梁无缺口冲击强度简支梁无缺口冲击强度 | |||
| 23℃23℃ | 57 | kJ/m2 | ISO 179/1eU |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火1.8 MPa，未退火 | 264 | ℃ | ISO 75-2/A |
| 熔融温度Melting Temperature 22 | 300 | ℃ | ISO 11357-3 |
| 线性热膨胀系数线性热膨胀系数 | |||
| TDTD | ISO 11359-2 | ||
| ---- | 5.7E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 到 23℃-40 to 23°C | 5.3E-5 | cm/cm/℃ | ISO 11359-2 |
| MDMD | ISO 11359-2 | ||
| ---- | 1.8E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 到 23℃-40 to 23°C | 2.0E-5 | cm/cm/℃ | ISO 11359-2 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 体积电阻率Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| 介电强度Electric Strength | 32 | kV/mm | IEC 60243-1 |
| 相对电容率Relative Permittivity | IEC 60250 | ||
| 100 Hz100 Hz | 4.40 | IEC 60250 | |
| 1 MHz1 MHz | 4.30 | IEC 60250 | |
| 耗散因数Dissipation Factor | IEC 60250 | ||
| 100 Hz100 Hz | 0.016 | IEC 60250 | |
| 1 MHz1 MHz | 0.019 | IEC 60250 | |
| 相比漏电起痕指数Comparative Tracking Index | 525 | V | IEC 60112 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 燃烧速率燃烧速率3 | |||
| 1 mm1.00 mm3 | 100 | mm/min | ISO 3795 |
| 极限氧指数Oxygen Index | 23 | % | ISO 4589-2 |
| FMVSS 阻燃等级FMVSS Flammability | B | FMVSS 302 | |