江苏普及塑料有限公司
| 牌号简介About |
|---|
| 35%玻璃纤维增强，ppa，高性能聚酰胺 |
产品描述Product Description
厂家：美国杜邦DuPont Canada, Inc. - Dartek Division
类别：PPAPPA
加工条件：注射成型Injection Molding
性能特点：热稳定性好;Heat Stabilized
填料：玻璃纤维 35
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.46 | g/cm3 | ISO 1183 |
| 收缩率Molding Shrinkage | |||
| MDMD | 0.30 | % | ISO 294-4 |
| TDTD | 0.90 | % | ISO 294-4 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸强度拉伸强度 | |||
| 23℃23°C | 187 | MPa | ISO 527-2 |
| 拉伸应变Tensile Elongation at Break | |||
| 断裂，23℃23°C | 2.10 | % | ISO 527-2 |
| 拉伸模量Tensile Modulus | |||
| 23℃23°C | 11600 | MPa | ISO 527-2 |
| 弯曲模量Flexural Modulus | |||
| 23℃23°C | 10300 | MPa | ISO 178 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Heat Deflection Temperature | |||
| 1.8 MPa，退火1.80MPa 退火 | 285 | ℃ | ISO 75-2/Af |
| 熔融温度Melting Temperature | 310 | ℃ | ISO 11357-3 |
| 维卡软化温度Vicat Softening Temperature | |||
| 线性热膨胀系数线膨胀系数 | |||
| MDMD | 2.1E-5 | 1/℃ | ISO 11359-2 |
| TDTD | 6.7E-5 | 1/℃ | ISO 11359-2 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 体积电阻体积电阻 | 1.0E+14 | Ω.cm | IEC 60093 |
| 绝缘强度绝缘强度 | |||
| 0.250 mm0.250 mm | 28 | KV/mm | IEC 60243-1 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级防火等级 | |||
| 0.75mm | HB | UL-94 | |
| 1.50mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 | |
| 灼热丝起燃温度灼热丝起燃温度 | |||
| 0.75 mm0.75mm | 775 | ℃ | IEC 60695-2-12 |
| 1.5 mm1.50mm | 725 | ℃ | IEC 60695-2-12 |
| 3 mm3.00mm | 775 | ℃ | IEC 60695-2-12 |
| 灼热丝相对温度灼热丝相对温度 | |||
| 0.75mm0.75mm | 750 | ℃ | IEC 60695-2-13 |
| 1.50mm1.50mm | 700 | ℃ | IEC 60695-2-13 |
| 3.00mm3.00mm | 850 | ℃ | IEC 60695-2-13 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁无缺口冲击强度Charpy Unnotched Impact Strength | |||
| 23℃23°C | 45 | kJ/m2 | ISO 179/1eU |
| -30℃-30°C | 40 | kJ/m2 | ISO 179/1eU |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | |||
| 23℃23°C | 8 | kJ/m2 | ISO 179/1eA |
| -30℃-30°C | 7 | kJ/m2 | ISO 179/1eA |