| 牌号简介About |
|---|
| 35%玻璃纤维增强，ppa，高性能聚酰胺 35% Glass Reinforced, PPA, High Performance Polyamide |
产品描述Product Description
厂家：美国杜邦DuPont Canada, Inc. - Dartek Division
类别：PPAPPA
加工条件：注射成型Injection Molding
性能特点：防火阻燃等级HB; 热稳定性好;Heat Stabilized,HB
填料：玻璃纤维 35
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40℃-40°C | 11 | kJ/m2 | ISO 179/1eA |
| -30℃-30°C | 10 | kJ/m2 | ISO 179/1eA |
| 23℃23°C | 11 | kJ/m2 | ISO 179/1eA |
| 简支梁无缺口冲击强度Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30℃-30°C | 60 | kJ/m2 | ISO 179/1eU |
| 23℃23°C | 70 | kJ/m2 | ISO 179/1eU |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | ISO 180/1A | ||
| -30℃-30°C | 10 | kJ/m2 | ISO 180-1A |
| 23℃23°C | 11 | kJ/m2 | ISO 180-1A |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火1.8 MPa，未退火 | 260 | ℃ | ISO 75-2/A |
| 0.45 MPa，未退火0.45 MPa，未退火 | 284 | ℃ | ISO 75-2/B |
| 熔融温度Melting Temperature 22 | 300 | ℃ | ISO 11357-3 |
| 线性热膨胀系数线性热膨胀系数 | |||
| TDTD | ISO 11359-2 | ||
| ---- | 5.5E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 到 23℃-40 to 23°C | 5.5E-5 | cm/cm/℃ | ISO 11359-2 |
| MDMD | ISO 11359-2 | ||
| ---- | 1.8E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 到 23℃-40 to 23°C | 1.8E-5 | cm/cm/℃ | ISO 11359-2 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 表面电阻率Surface Resistivity | -- | ohms | IEC 60093 |
| 体积电阻率Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| 介电强度Electric Strength | 36 | kV/mm | IEC 60243-1 |
| 相对电容率Relative Permittivity | IEC 60250 | ||
| 100 Hz100 Hz | 4.00 | IEC 60250 | |
| 1 MHz1 MHz | 4.00 | IEC 60250 | |
| 相比漏电起痕指数Comparative Tracking Index | 600 | V | IEC 60112 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 燃烧速率燃烧速率3 | |||
| 1 mm1.00 mm3 | 23 | mm/min | ISO 3795 |
| 阻燃等级Flame Rating | UL 94 | ||
| 0.90 mm0.9 mm | HB | UL 94 | |
| 1.50 mm1.5 mm | HB | UL 94 | |
| 可燃性等级Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.9 mm0.9 mm | HB | IEC 60695-11-10, -20 | |
| 1.5 mm1.5 mm | HB | IEC 60695-11-10, -20 | |
| 极限氧指数Oxygen Index | 24 | % | ISO 4589-2 |
| FMVSS 阻燃等级FMVSS Flammability | B | FMVSS 302 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| OdorOdor | 4.00 | VDA 270 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量Tensile Modulus | 12000 | MPa | ISO 527-2 |
| 拉伸强度拉伸强度 | |||
| 断裂断裂 | 210 | MPa | ISO 527-2 |
| 拉伸应变拉伸应变 | |||
| 断裂断裂 | 2.4 | % | ISO 527-2 |
| Tensile Creep Modulus（1 hr）Tensile Creep Modulus (1 hr) | -- | MPa | ISO 899-1 |
| 拉伸蠕变模量拉伸蠕变模量 | |||
| 1000 hr1000 hr | -- | MPa | ISO 899-1 |
| 弯曲模量Flexural Modulus | 10300 | MPa | ISO 178 |
| 弯曲强度Flexural Stress | 300 | MPa | ISO 178 |
| 泊松比Poisson's Ratio | 0.39 | ISO 527 | |
| 洛氏硬度Rockwell Hardness | ISO 2039-2 | ||
| M 级M-Scale | 108 | ISO 2039-2 | |
| R 级R-Scale | 124 | ISO 2039-2 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Density | 1.47 | g/cm3 | ISO 1183 |
| 收缩率Molding Shrinkage | ISO 294-4 | ||
| TDAcross Flow | 0.60 | % | ISO 294-4 |
| MDFlow | 0.20 | % | ISO 294-4 |
| 吸水率吸水率 | |||
| 饱和，23℃，2.00 mmSaturation，23℃，2.00 mm | 4.5 | % | ISO 62 |
| Specific Heat Capacity of MeltSpecific Heat Capacity of Melt | 1860 | J/kg/℃ | |
| Thermal Conductivity of MeltThermal Conductivity of Melt | 0.25 | W/m/K | |