Plexiglas? 8N

聚甲基丙烯酸甲酯-丙烯酸

Evonik Industries AG

产品说明：

Product Profile:
PLEXIGLAS? 8N is an amorphous thermoplastic molding compound (PMMA).

Typical properties of PLEXIGLAS? molding compounds are:

good flow

high mechanical strength, surface hardness and abrasion resistance

high light transmission

very good weather resistance

free colorability due to crystal clarity

Special properties of PLEXIGLAS? 8N are:

optimum mechanical properties

maximum heat deflection temperature

good flow / melt viscosity

AMECA listing.

Application:
Used for injection molding optical and technical items.

Examples:
optical waveguides, luminaire covers, automotive lighting, instrument cluster covers, optical lenses, displays, etc.

特性	高强度良好的流动性良好的着色性良好耐磨损性耐气候影响性能良好无定形的硬度高
用途	Automotive Backlights Displays 保护性遮盖物光学应用镜头汽车领域的应用
形式	粒子
加工方法	注射成型
多点数据	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)

物理性能	额定值	单位制	测试方法
密度	1.19	g/cm3	ISO 1183
溶化体积流率（MVR）(230°C/3.8 kg)	3.00	cm3/10min	ISO 1133

机械性能	额定值	单位制	测试方法
拉伸模量	3300	MPa	ISO 527-2/1
拉伸应力(断裂)	77.0	MPa	ISO 527-2/5
拉伸应变(断裂)	5.5	%	ISO 527-2/5

冲击性能	额定值	单位制	测试方法
简支梁无缺口冲击强度(23°C)	20	kJ/m2	ISO 179/1eU

热性能	额定值	单位制	测试方法
热变形温度
0.45 MPa, 未退火	103	°C	ISO 75-2/B
1.8 MPa, 未退火	98.0	°C	ISO 75-2/A
玻璃转化温度	117	°C	ISO 11357-2
维卡软化温度	108	°C	ISO 306/B50
线形热膨胀系数 - 流动(0 到 50°C)	8.0E-5	cm/cm/°C	ISO 11359-2

可燃性	额定值		测试方法
UL 阻燃等级(1.60 mm)	HB		UL 94
Fire Rating	B2		DIN 4102

光学性能	额定值	单位制	测试方法
折射率	1.490		ISO 489
透射率1	92.0	%	ISO 13468-2
雾度	0.50	%	ASTM D1003

注射	额定值	单位制
干燥温度	98.0	°C
干燥时间	2.0 到 3.0	hr
加工（熔体）温度	220 到 260	°C
模具温度	60.0 到 90.0	°C

备注
1 .	D65