东莞市铭汇塑胶有限公司
Plexiglas? Resist zk6BR
聚甲基丙烯酸甲酯-丙烯酸
Evonik Industries AG
产品说明:
Product Profile:
PLEXIGLAS? Resist zk6BR is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).
Typical properties of impact-modified
PLEXIGLAS? molding compounds are:
PLEXIGLAS? Resist zk6BR is characterized by the
following special properties:
Application:
Used for extruding and coextruding sheets and profiles as well as for injection molding
Examples:
extruded and injection-molded luminaire covers, extruded hollow profiles, writing utensils such as stencils and fountain pens,
appliance housings, coextruded profiles for window frames, gutters, downspouts, and housewares such as cutlery handles, bowls,
PLEXIGLAS? Resist zk6BR is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).
Typical properties of impact-modified
PLEXIGLAS? molding compounds are:
- high weather resistance
- excellent transmission and clarity
- brilliant appearance
- the pleasant feel and sound of the moldings.
PLEXIGLAS? Resist zk6BR is characterized by the
following special properties:
- maximum break resistance and impact strength,
- improved resistance to stress cracking
- balanced property profile
- AMECA listing.
Application:
Used for extruding and coextruding sheets and profiles as well as for injection molding
Examples:
extruded and injection-molded luminaire covers, extruded hollow profiles, writing utensils such as stencils and fountain pens,
appliance housings, coextruded profiles for window frames, gutters, downspouts, and housewares such as cutlery handles, bowls,
添加剂 |
|
特性 |
|
用途 |
|
加工方法 |
|
多点数据 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
密度 | 1.16 | g/cm3 | ISO 1183 |
溶化体积流率(MVR)(230°C/3.8 kg) | 1.60 | cm3/10min | ISO 1133 |
吸水率 | ISO 62 | ||
23°C, 24 hr | 1.8 | % | ISO 62 |
平衡, 23°C, 50% RH | 0.50 | % | ISO 62 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸模量 | 1800 | MPa | ISO 527-2/1 |
拉伸应力(屈服) | 45.0 | MPa | ISO 527-2/50 |
拉伸应变(屈服) | 5.0 | % | ISO 527-2/50 |
标称拉伸断裂应变 | 54 | % | ISO 527-2 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
简支梁无缺口冲击强度(23°C) | 80 | kJ/m2 | ISO 179/1eU |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
热变形温度 | |||
0.45 MPa, 未退火 | 93.0 | °C | ISO 75-2/B |
1.8 MPa, 未退火 | 88.0 | °C | ISO 75-2/A |
玻璃转化温度 | 109 | °C | ISO 11357-2 |
维卡软化温度 | 95.0 | °C | ISO 306/B50 |
线形热膨胀系数 - 流动(0 到 50°C) | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
可燃性 | 额定值 | 测试方法 | |
---|---|---|---|
UL 阻燃等级(1.60 mm) | HB | UL 94 | |
Fire Rating | B2 | DIN 4102 |
光学性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
折射率 | 1.490 | ISO 489 | |
透射率1 | 91.0 | % | ISO 13468-2 |
雾度 | 2.0 | % | ASTM D1003 |
注射 | 额定值 | 单位制 | |
---|---|---|---|
干燥温度 | 85.0 | °C | |
干燥时间 | 2.0 到 3.0 | hr | |
加工(熔体)温度 | 220 到 260 | °C | |
模具温度 | 50.0 到 70.0 | °C |
备注 | |
---|---|
1 . | D65 |