| 概述：CZL-2000是一种沥青基碳纤维和聚四氟乙烯填充PPS化合物，具有优异的自润滑性能，低磨损，低摩擦性能。颜色：布莱克 Outline: CZL-2000 is a pitch based carbon fiber and poly tetra fluoro ethylene filled PPS compound that has excellent self lubricant performance with low wear, and low friction properties. Color: Black |
产品描述Product Description
厂家：日本大日本油墨DIC Corporation
类别：PPSPPS
颜色：黑色
加工条件：注射成型Injection Molding
性能特点：防火阻燃等级V-0; 自润滑; 耐磨; 低摩擦系数;Low coefficient of friction,Self-lubricating,Good wear resistance,V-0
填料：PTFE/碳纤维
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.52 | g/cm3 | ASTM D792 |
| 收缩率Molding Shrinkage | ASTM D955 | ||
| MD流动 | 0.25 | % | ASTM D955 |
| TD横向流动 | 0.25 | % | ASTM D955 |
| 吸水率吸水率 | |||
| 23℃，24hr23℃，24 hr | 0.070 | % | ASTM D570 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | 45 | J/m | ASTM D256 |
| 悬臂梁无缺口冲击强度Unnotched Izod Impact (Area) | 200 | J/m | ASTM D256 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火1.8 MPa，未退火 | 265 | ℃ | ASTM D648 |
| 线性热膨胀系数CLTE | ASTM D696 | ||
| MD：-30~90℃Flow : -22 to 194°F | 2.1E-5 | 1/℃ | ASTM D696 |
| TD：-30~90℃Transverse : -22 to 194°F | 2.1E-5 | 1/℃ | ASTM D696 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 体积电阻率Volume Resistivity | 1.0E+7 到 1.0E+8 | ohms·cm | ASTM D257 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 0.80 mm0.8 mm | V-0 | UL 94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 洛氏硬度Rockwell Hardness | ASTM D785 | ||
| M 级M 级 | 98 | ASTM D785 | |
| R 级R 级 | 118 | ASTM D785 | |
| 拉伸模量Tensile Modulus | 8500 | MPa | ASTM D638 |
| 拉伸强度Tensile Strength | 100 | MPa | ASTM D638 |
| 拉伸应变拉伸应变 | |||
| 断裂断裂 | 0.80 | % | ASTM D638 |
| 弯曲模量Flexural Modulus | 8000 | MPa | ASTM D790 |
| 弯曲强度Flexural Strength | 110 | MPa | ASTM D790 |
| 压缩强度Compressive Strength | 120 | MPa | ASTM D695 |
| 泊松比Poisson's Ratio | 0.36 | ||
| 摩擦系数Coefficient of Friction 22 | ASTM D1894 | ||
| 与钢 - 动态vs. Steel - Dynamic | 0.21 | ASTM D1894 | |
| 与钢 - 静态与钢 - 静态 | 0.21 | ASTM D1894 | |