| 概述：FZ-8600是一种玻璃纤维和矿物填充的聚苯硫醚化合物，开发的目的是为灯罩提供良好的表面平整度和光泽。颜色：布莱克 Outline: FZ-8600 is a glass fiber and mineral filled PPS compound developed to provide excellent surface flatness and luster for lamp reflectors. Color: Black |
产品描述Product Description
厂家：日本大日本油墨DIC Corporation
类别：PPSPPS
颜色：黑色
加工条件：注射成型Injection Molding
性能特点：表面光泽度好;Good surface appearance
填料：玻璃纤维/矿物
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.90 | g/cm3 | ASTM D792 |
| 收缩率Molding Shrinkage | |||
| MDMD | 0.40 | % | ASTM D995 |
| TDTD | 1.00 | % | ASTM D995 |
| 吸水率Water Absorption | |||
| 23℃，24hr(23°C, 24 hr) | 0.02 | % | ASTM D570 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Heat Deflection Temperature | |||
| 1.8 MPa，未退火1.80MPa 未退火 | 260 | ℃ | ASTM D648 |
| 线性热膨胀系数线膨胀系数 | |||
| MDMD | 1.8E-5 | 1/℃ | ASTM D696 |
| TDTD | 1.8E-5 | 1/℃ | ASTM D696 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 体积电阻体积电阻 | 1.0E+16 | Ω.cm | ASTM D257 |
| 绝缘强度绝缘强度 | |||
| 1.60 mm1.60 mm | 16 | KV/mm | ASTM D149 |
| 介电常数Dielectric Constant | |||
| 23℃23°C | 5.0 | 1 MHz | ASTM D150 |
| 耗散因数Dissipation Factor | |||
| 23℃ 23°C | 6.0E-3 | 1 MHz | ASTM D150 |
| 耐电弧性Arc Resistance | 160 | sec | ASTM D495 |
| 相比漏电起痕指数相对漏电起痕指数 | 190 | V | ASTM D3638 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级防火等级 | |||
| 0.800 mm | V-0 | UL 94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | |||
| 23℃23°C | 50 | J/m | ASTM D256 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 洛氏硬度Rockwell Hardness | 100 | M 级 | ASTM D785 |
| 洛氏硬度Rockwell Hardness | 120 | R 级 | ASTM D785 |
| 拉伸强度拉伸强度 | |||
| 23℃23°C | 100 | MPa | ASTM D638 |
| 拉伸应变Tensile Elongation at Break | |||
| 断裂，23℃23°C | 1.1 | % | ASTM D638 |
| 泊松比Poisson's Ratio | 0.33 | ASTM E132 | |
| 拉伸模量Tensile Modulus | |||
| 23℃23°C | 12500 | MPa | ASTM D638 |
| 弯曲强度Flexural Strength | |||
| 23℃23°C | 140 | MPa | ASTM D790 |
| 弯曲模量Flexural Modulus | |||
| 23℃23°C | 12000 | MPa | ASTM D790 |
| 磨擦系数磨擦系数 | |||
| 动态动态 | 0.35 | ASTM D3702 | |
| 静态静态 | 0.35 | ASTM D3702 | |