| 牌号简介About |
|---|
| 概述：FZ-1130-D5是一种玻璃纤维增强聚苯硫醚化合物，与传统牌号相比，闪光减少，柔韧性提高。颜色：黑色和自然色（棕色）。 Outline: FZ-1130-D5 is a glass fiber 30% reinforced polyphenylene sulfide compound with reduced flash and improved flexibility compared to conventional grades. Color: Black and Natural (Brown). |
产品描述Product Description
厂家：日本大日本油墨DIC Corporation
类别：PPSPPS
颜色：黑色,自然色
加工条件：注射成型Injection Molding
性能特点：防火阻燃等级V-0; 韧性好;Good flexibility,V-0
填料：玻璃纤维
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.56 | g/cm3 | ASTM D792 |
| 收缩率Molding Shrinkage | ASTM D955 | ||
| MD流动 | 0.27 | % | ASTM D955 |
| TD横向流动 | 1.2 | % | ASTM D955 |
| 吸水率吸水率 | |||
| 23℃，24hr23℃，24 hr | 0.020 | % | ASTM D570 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | 95 | J/m | ASTM D256 |
| 悬臂梁无缺口冲击强度Unnotched Izod Impact (Area) | 550 | J/m | ASTM D256 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火1.8 MPa，未退火 | 265 | ℃ | ASTM D648 |
| 线性热膨胀系数CLTE | ASTM D696 | ||
| MD：-30~90℃Flow : -22 to 194°F | 2.3E-5 | 1/℃ | ASTM D696 |
| TD：-30~90℃Transverse : -22 to 194°F | 2.3E-5 | 1/℃ | ASTM D696 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 体积电阻率Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| 介电强度介电强度 | |||
| 1.6 mm1.60 mm | 16 | kV/mm | ASTM D149 |
| 介电常数介电常数 | |||
| 1 MHz1 MHz | 4.00 | ASTM D150 | |
| 耗散因数耗散因数 | |||
| 1 MHz1 MHz | 2.0E-3 | ASTM D150 | |
| 耐电弧性Arc Resistance | 120 | sec | ASTM D495 |
| 相比漏电起痕指数Comparative Tracking Index | 170 | V | ASTM D3638 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 0.80 mm0.8 mm | V-0 | UL 94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 洛氏硬度Rockwell Hardness | ASTM D785 | ||
| M 级M 级 | 100 | ASTM D785 | |
| R 级R 级 | 121 | ASTM D785 | |
| 拉伸模量Tensile Modulus | 11000 | MPa | ASTM D638 |
| 拉伸强度Tensile Strength | 175 | MPa | ASTM D638 |
| 拉伸应变拉伸应变 | |||
| 断裂断裂 | 1.9 | % | ASTM D638 |
| 弯曲模量Flexural Modulus | 10000 | MPa | ASTM D790 |
| 弯曲强度Flexural Strength | 240 | MPa | ASTM D790 |
| 压缩强度Compressive Strength | 190 | MPa | ASTM D695 |
| 泊松比Poisson's Ratio | 0.36 | ||
| 摩擦系数Coefficient of Friction 33 | ASTM D1894 | ||
| 与钢 - 动态vs. Steel - Dynamic | 0.35 | ASTM D1894 | |
| 与钢 - 静态与钢 - 静态 | 0.35 | ASTM D1894 | |
| 断裂弯曲伸长率Flexural Elongation at Break | 2.5 | % | ASTM D790 |