一种具有抗冲击性能的共聚物树脂,用于需要很高抗冲击强度的消费品和工业产品。 An impact copolymer resin designed for consumer and industrial products requiring very high impact resistance. |
产品描述Product Description
厂家:美国埃克森美孚ExxonMobil Chemical
类别:PP共聚PP copolymer
用途:家电部件;电池盒;工业应用;玩具;硬包装;消费品应用领域;
加工条件:注射成型Injection Molding
性能特点:机械强度好; 刚性韧性平衡; 流动性中等; 冲击性能好;Good Rigidity,High impact resistance,Moderate liquidity,Rigid-tough balance
技术参数Technical Data | |||
---|---|---|---|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
密度Density | 0.900 | g/cm3 | ExxonMobil Method |
熔体质量流动速率熔体质量流动速率 | |||
230℃,2.16kg230℃/2.16 kg | 4.0 | g/10min | ASTM D1238 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
简支梁缺口冲击强度Charpy Notched Impact Strength | |||
-30℃-30°C | 6.8 | kJ/m2 | |
23℃23°C | 57 | kJ/m2 | |
悬臂梁缺口冲击强度Notched Izod Impact Strength | |||
23℃23°C | 无断裂 | ASTM D256A | |
-40℃-40°C | 9.0 | kJ/m2 | ISO 180-1A |
-18℃-18°C | 11 | kJ/m2 | ISO 180-1A |
23℃23°C | 53 | kJ/m2 | ISO 180-1A |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
热变形温度Deflection Temperature Under Load | |||
0.45 MPa,未退火66 psi, Unannealed | 90.6 | ℃ | ASTM D648 |
0.45 MPa,未退火66 psi, Unannealed | 82.0 | ℃ | ISO 75-2/Bf |
0.45 MPa,退火66 psi, Annealed | 112 | ℃ | ASTM D648 |
1.8 MPa,未退火264 psi, Unannealed | 50.2 | ℃ | ISO 75-2/A |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
洛氏硬度Rockwell Hardness | 84 | ASTM D785 | |
拉伸模量Tensile Modulus | 1200 | MPa | ISO 527-1-2 |
拉伸强度Tensile Strength | |||
屈服屈服33 | 23.7 | MPa | ASTM D638 |
屈服Yield | 23.0 | MPa | ISO 527-2/50 |
拉伸应变Tensile Elongation | |||
屈服屈服33 | 6.0 | % | ASTM D638 |
屈服Yield | 5.6 | % | ISO 527-2/50 |
弯曲模量Flexural Modulus | |||
1% 正割1% 正割 44 | 1210 | MPa | ASTM D790-A |
1% 正割1% 正割 55 | 1300 | MPa | ASTM D790-B |
----66 | 1140 | MPa | ISO 178 |