| 牌号简介About |
|---|
| 一种具有高熔体流动速率、中等抗冲击强度的共聚物树脂，用于需要较短周期时间和低气味的薄壁注塑成型。 A high melt flow rate medium impact copolymer resin designed for thin wall injection molding requiring fast cycle time and low odor. |
产品描述Product Description
厂家：美国埃克森美孚ExxonMobil Chemical
类别：PP共聚PP copolymer
用途：食品硬包装;家电部件;玩具;容器;消费品应用领域;
颜色：自然色
加工条件：注射成型Injection Molding
性能特点：成核的; 机械强度好; 含脱模剂; 低VOC; 流动性高; 冲击性能好;Good Rigidity,High impact resistance,High liquidity,Nucleation,Good stripping performance,Low odor
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 熔体质量流动速率熔体质量流动速率 | |||
| 230℃，2.16kg230℃/2.16 kg | 50 | g/10min | ASTM D1238 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃-30°C | 4.2 | kJ/m2 | ISO 179/1eA |
| -20℃-20°C | 4.6 | kJ/m2 | ISO 179/1eA |
| 0℃0°C | 5.4 | kJ/m2 | ISO 179/1eA |
| 23℃23°C | 8.5 | kJ/m2 | ISO 179/1eA |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | |||
| 23℃23°C | 94 | J/m | ASTM D256-A |
| -40℃-40°C | 3.9 | kJ/m2 | ISO 180-1A |
| -18℃-18°C | 4.2 | kJ/m2 | ISO 180-1A |
| 23℃23°C | 7.4 | kJ/m2 | ISO 180-1A |
| 落锤冲击落锤冲击7 | |||
| -29℃，3.18 mm-29℃，3.18 mm7 | 16.6 | J | ASTM D5420 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Deflection Temperature Under Load | |||
| 0.45 MPa，未退火66 psi, Unannealed | 105 | ℃ | ASTM D648 |
| 0.45 MPa，未退火66 psi, Unannealed | 93.0 | ℃ | ISO 75-2/Bf |
| 0.45 MPa，退火66 psi, Annealed | 119 | ℃ | ASTM D648 |
| 1.8 MPa，未退火264 psi, Unannealed | 50.7 | ℃ | ISO 75-2/A |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 洛氏硬度Rockwell Hardness | 89 | ASTM D785 | |
| 拉伸模量Tensile Modulus | 1370 | MPa | ISO 527-1-2 |
| 拉伸强度Tensile Strength | |||
| 屈服屈服 33 | 25.4 | MPa | ASTM D638 |
| 屈服Yield | 24.7 | MPa | ISO 527-2/50 |
| 拉伸应变Tensile Elongation | |||
| 屈服屈服 33 | 4.6 | % | ASTM D638 |
| 屈服Yield | 3.7 | % | ISO 527-2/50 |
| 弯曲模量Flexural Modulus | |||
| 1% 正割1% Secant 44 | 1340 | MPa | ASTM D790-A |
| 1% 正割1% Secant 55 | 1520 | MPa | ASTM D790-B |
| ---- 66 | 1270 | MPa | ISO 178 |