| 牌号简介About |
|---|
| 20%玻璃纤维增强，增韧，阻燃，聚对苯二甲酸丁二醇酯，具有改进的抗冲击性 20% Glass Reinforced, Toughened, Flame Retardant, Polybutylene Terephthalate with Improved Impact Resistance |
产品描述Product Description
厂家：美国杜邦DuPont Canada, Inc. - Dartek Division
类别：PBTpolybutylene terephthalate
加工条件：片材挤出成型
性能特点：防火阻燃等级V-0; 阻燃; 冲击性能好;High impact resistance,Flame Characteristics,V-0
填料：玻璃纤维 20
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量Tensile Modulus | 5800 | MPa | ISO 527-2 |
| 拉伸强度拉伸强度 | |||
| 断裂断裂 | 90.0 | MPa | ISO 527-2 |
| 拉伸应变拉伸应变 | |||
| 断裂断裂 | 4.2 | % | ISO 527-2 |
| Tensile Creep Modulus（1 hr）Tensile Creep Modulus (1 hr) | 5400 | MPa | ISO 899-1 |
| 拉伸蠕变模量拉伸蠕变模量 | |||
| 1000 hr1000 hr | 3500 | MPa | ISO 899-1 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃-30°C | 8.4 | kJ/m2 | ISO 179/1eA |
| 23℃23°C | 10 | kJ/m2 | ISO 179/1eA |
| 简支梁无缺口冲击强度Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30℃-30°C | 60 | kJ/m2 | ISO 179/1eU |
| 23℃23°C | 55 | kJ/m2 | ISO 179/1eU |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 8.0 MPa，未退火8.0 MPa，未退火 | 120 | ℃ | ISO 75-2/C |
| 1.8 MPa，未退火1.8 MPa，未退火 | 180 | ℃ | ISO 75-2/A |
| 维卡软化温度维卡软化温度 | |||
| B50B50 | 185 | ℃ | ISO 306 |
| 熔融温度Melting Temperature 22 | 205 | ℃ | ISO 11357-3 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 表面电阻率Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| 体积电阻率Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| 介电强度Electric Strength | 27 | kV/mm | IEC 60243-1 |
| 相对电容率Relative Permittivity | IEC 60250 | ||
| 100 Hz100 Hz | 4.10 | IEC 60250 | |
| 1 MHz1 MHz | 3.90 | IEC 60250 | |
| 耗散因数Dissipation Factor | IEC 60250 | ||
| 100 Hz100 Hz | 0.012 | IEC 60250 | |
| 1 MHz1 MHz | 0.017 | IEC 60250 | |
| 相比漏电起痕指数Comparative Tracking Index | 275 | V | IEC 60112 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级Flame Rating | UL 94 | ||
| 1.50 mm1.5 mm | V-0 | UL 94 | |
| 3.00 mm3.0 mm | V-0 | UL 94 | |
| 可燃性等级Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.5 mm1.5 mm | V-0 | IEC 60695-11-10, -20 | |
| 3.0 mm3.0 mm | V-0 | IEC 60695-11-10, -20 | |
| 极限氧指数Oxygen Index | 30 | % | ISO 4589-2 |
| FMVSS 阻燃等级FMVSS Flammability | DNI | FMVSS 302 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Density | 1.60 | g/cm3 | ISO 1183 |
| 熔体体积流动速率熔体体积流动速率 | |||
| 250℃，2.16 kg250℃/2.16 kg | 10.0 | cm3/10min | ISO 1133 |
| 收缩率Molding Shrinkage | ISO 294-4 | ||
| TDAcross Flow | 1.0 | % | ISO 294-4 |
| MDFlow | 0.40 | % | ISO 294-4 |
| 吸水率吸水率 | |||
| 饱和，23℃，2.00 mmSaturation，23℃，2.00 mm | 0.30 | % | ISO 62 |
| 平衡，23℃，50% RH，2.00 mmEquilibrium，23℃，2.00 mm，50% RH | 0.15 | % | ISO 62 |
| 熔体密度Melt Density | 1.32 | g/cm3 | |
| 顶出温度Ejection Temperature | 150 | ℃ | |
| Specific Heat Capacity of MeltSpecific Heat Capacity of Melt | 1850 | J/kg/℃ | |
| Thermal Conductivity of MeltThermal Conductivity of Melt | 0.25 | W/m/K | |