江苏普及塑料有限公司
| 牌号简介About |
|---|
| 30%玻璃纤维增强，抗水解，聚对苯二甲酸丁二醇酯 30% Glass Reinforced, Hydrolysis Resistant, Polybutylene Terephthalate |
产品描述Product Description
厂家：美国杜邦DuPont Canada, Inc. - Dartek Division
类别：PBTpolybutylene terephthalate
加工条件：注射成型Injection Molding
性能特点：防火阻燃等级HB; 耐水解;Hydrolysis stability,HB
填料：玻璃纤维 30
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量Tensile Modulus | 8500 | MPa | ISO 527-2 |
| 拉伸强度拉伸强度 | |||
| 断裂断裂 | 132 | MPa | ISO 527-2 |
| 拉伸应变拉伸应变 | |||
| 断裂断裂 | 3.5 | % | ISO 527-2 |
| 弯曲模量Flexural Modulus | 7700 | MPa | ISO 178 |
| 弯曲强度Flexural Stress | 200 | MPa | ISO 178 |
| 泊松比Poisson's Ratio 33 | 0.34 | ISO 527 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃-30°C | 12 | kJ/m2 | ISO 179/1eA |
| 23℃23°C | 13 | kJ/m2 | ISO 179/1eA |
| 简支梁无缺口冲击强度简支梁无缺口冲击强度 | |||
| 23℃23℃ | 70 | kJ/m2 | ISO 179/1eU |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | ISO 180/1A | ||
| -40℃-40°C | 11 | kJ/m2 | ISO 180-1A |
| 23℃23°C | 14 | kJ/m2 | ISO 180-1A |
| 悬臂梁无缺口冲击强度悬臂梁无缺口冲击强度 | |||
| 23℃23℃ | 65 | kJ/m2 | ISO 180/1U |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火1.8 MPa，未退火 | 207 | ℃ | ISO 75-2/A |
| 0.45 MPa，未退火0.45 MPa，未退火 | 221 | ℃ | ISO 75-2/B |
| 维卡软化温度维卡软化温度 | |||
| B50B50 | 215 | ℃ | ISO 306 |
| 熔融温度Melting Temperature 55 | 225 | ℃ | ISO 11357-3 |
| 线性热膨胀系数线性热膨胀系数 | |||
| TDTD | ISO 11359-2 | ||
| ---- | 1.5E-4 | cm/cm/℃ | ISO 11359-2 |
| -40 到 23℃-40 to 23°C | 9.0E-5 | cm/cm/℃ | ISO 11359-2 |
| 55 到 160℃55 to 160°C | 1.5E-4 | cm/cm/℃ | ISO 11359-2 |
| MDMD | ISO 11359-2 | ||
| ---- | 2.0E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 到 23℃-40 to 23°C | 2.5E-5 | cm/cm/℃ | ISO 11359-2 |
| 55 到 160℃55 to 160°C | 1.5E-5 | cm/cm/℃ | ISO 11359-2 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 表面电阻率Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| 体积电阻率Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| 介电强度Electric Strength | IEC 60243-1 | ||
| ---- | 44 | kV/mm | IEC 60243-1 |
| 1 mm1.00 mm 55 | 31 | kV/mm | IEC 60243-1 |
| 相对电容率Relative Permittivity | IEC 60250 | ||
| 100 Hz100 Hz | 4.40 | IEC 60250 | |
| 1 MHz1 MHz | 4.10 | IEC 60250 | |
| 耗散因数Dissipation Factor | ASTM D150 | ||
| 100 Hz100 Hz | 2.5E-3 | ASTM D150 | |
| 1 kHz1 kHz | 7.0E-3 | ASTM D150 | |
| 1 MHz1 MHz | 0.020 | ASTM D150 | |
| 耗散因数Dissipation Factor | IEC 60250 | ||
| 100 Hz100 Hz | 2.5E-3 | IEC 60250 | |
| 1 MHz1 MHz | 0.020 | IEC 60250 | |
| 相比漏电起痕指数Comparative Tracking Index | 450 | V | IEC 60112 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级0.75 mm | |||
| 0.75 mm | HB | UL 94 | |
| 燃烧速率燃烧速率6 | |||
| 1 mm1.00 mm6 | 30 | mm/min | ISO 3795 |
| 可燃性等级可燃性等级 | |||
| 0.75 mm0.75 mm | HB | IEC 60695-11-10, -20 | |
| 极限氧指数Oxygen Index | 19 | % | ISO 4589-2 |
| FMVSS 阻燃等级FMVSS Flammability | B | FMVSS 302 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Density | 1.50 | g/cm3 | ISO 1183 |
| 收缩率Molding Shrinkage | ISO 294-4 | ||
| TDAcross Flow | 1.0 | % | ISO 294-4 |
| MDFlow | 0.30 | % | ISO 294-4 |
| 吸水率吸水率 | |||
| 饱和，23℃，2.00 mmSaturation，23℃，2.00 mm | 0.35 | % | ISO 62 |
| 平衡，23℃，50% RH，2.00 mmEquilibrium，23℃，2.00 mm，50% RH | 0.15 | % | ISO 62 |
| 粘数Viscosity Number | 95.0 | cm3/g | ISO 307 |
| Flow Length（2.00 mm）Flow Length 2 (2.00 mm)2 | 350 | mm | |
| 熔体密度Melt Density | 1.29 | g/cm3 | |
| 顶出温度Ejection Temperature | 170 | ℃ | |
| Specific Heat Capacity of MeltSpecific Heat Capacity of Melt | 1730 | J/kg/℃ | |
| Thermal Conductivity of MeltThermal Conductivity of Melt | 0.28 | W/m/K | |