产品描述Product Description
厂家：日本出光Idemitsu Kosan Co., Ltd.
类别：PCPolycarbonate
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 收缩率收缩率 | |||
| MD：1.6 mmflow direction，1.6 mm | 0.5 ~ 0.7 | % | ISO 294 |
| 密度Density | 1.200 | g/cm3 | ISO 1183 B |
| 熔体质量流动速率熔体质量流动速率 | |||
| 300℃，1.20kg300℃; 1.2 kg | 18 | g/10min | ISO 1133 |
| 吸水率吸水率 | |||
| 23℃，24hr，60% RH23℃; 24 h，50% rh | 0.23 | % | ISO 62 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸强度拉伸强度 | |||
| 断裂断裂 | 65 | MPa | ISO 527 |
| 屈服屈服 | 65 | MPa | ISO 527 |
| 标称拉伸断裂应变Nominal Tensile Strain at Break | 95 | % | ISO 527 |
| 拉伸模量张力弹性模量 | 2.000 | Mpa | ISO 527 |
| 弯曲强度Flexural Strength | 90 | MPa | ISO 178 |
| 弯曲模量Flexural Modulus | 2.300 | MPa | ISO 178 |
| 洛氏硬度Rockwell Hardness | 120/50 | R/M 级 | ISO 2039 |
| 泰伯耐磨性Taber Abrasion Resistance | 12 | mg (1000 rounds) | ASTM D1044 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 维卡软化温度维卡软化温度 | |||
| A50A/10N | 145 | ℃ | ISO 306 |
| 热变形温度热变形温度 | |||
| 1.8 MPa1.8MPa | 125 | ℃ | ISO 75 A |
| 线性热膨胀系数Linear Expansion Coefficient | 6.5 | x 10 -5 cm/cm/oC | ASTM D 696 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 介电常数Dielectric Constant | 2.85 | 1 MHz | IEC 60250 |
| 介电常数Dielectric Constant | 2.91 | 60 Hz | IEC 60250 |
| 介电强度介电强度 | |||
| 1.6 mm1.6 mm | 30E+5 | kV/mm | IEC 60243-1 |
| 耗散因数Dissipation Factor | 0.0092 | 1 MHz | IEC 250 |
| 耐电弧性Arc Resistance | 110 | sec | ASTM D495 |
| 体积电阻率Volume Resistivity | 10^16 | ohms·cm | IEC 60093 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级阻燃等级 | V-0 | 1.5mm | UL 94 |
| 极限氧指数Oxygen Index | 26 | % | ASTM D2863 |
| 灼热丝起燃温度热灯丝点火测试 (GWIT) 1.60 mm | |||
| 1.6 mm | 960 | ℃ | IEC 60695-2-13 |
| 灼热丝起燃温度热灯丝点火测试 (GWIT) 2.00 mm | |||
| 2 mm | 960 | ℃ | IEC 60695-2-13 |
| 灼热丝起燃温度热灯丝点火测试 (GWIT) 3.00 mm | |||
| 3 mm | 960 | ℃ | IEC 60695-2-13 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁无缺口冲击强度简支梁无缺口冲击强度 at 23°C | |||
| 23℃ | 80 | kJ/m2 | ISO 179 |