| 牌号简介About |
|---|
| Lupoy PC 1300-03树脂专为挤出和注塑产品设计。它在耐热性、透明度和冲击强度方面表现出良好的物理性能平衡。 LUPOY PC 1300-03 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. |
产品描述Product Description
厂家：韩国LG化学LG Polymers India Pvt. Ltd.
类别：PCPolycarbonate
用途：包装;复合;电器用具;
加工条件：注射成型Injection Molding
性能特点：防火阻燃等级HB; 高粘度; 防火阻燃等级V-2; 耐高温; 透光性好; 冲击性能好;Good Clarity,High impact resistance,High Viscosity,High Heat Resistance,HB,V-2
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.20 | g/cm3 | ASTM D792 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 300℃，1.20kg300℃/1.2 kg | 3.0 | g/10min | ASTM D1238 |
| 收缩率收缩率 | |||
| MDMD | 0.50 to 0.70 | % | ASTM D955 |
| 吸水率吸水率 | |||
| 平衡，23℃，50% RH平衡，23℃，50% RH | 0.32 | % | ASTM D570 |
| 23℃，24hr23℃，24 hr | 0.15 | % | ASTM D570 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 悬臂梁缺口冲击强度悬壁梁缺口冲击强度 | |||
| 23℃，3.2mm23℃，3.20 mm4 | 950 | J/m | ASTM D256 |
| 23℃23℃ | No Break | ASTM D256 | |
| 装有测量仪表的落镖冲击装有测量仪表的落镖冲击5 | |||
| 23℃，3.20 mm，Total Energy23℃，3.20 mm，Total Energy5 | 94.0 | J | ASTM D3763 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，退火，4.0 mm1.8 MPa，退火，4.00 mm | 143 | ℃ | ASTM D648 |
| 1.8 MPa，未退火，4.0 mm1.8 MPa，未退火，4.00 mm | 132 | ℃ | ASTM D648 |
| 0.45 MPa，退火，4.0 mm0.45 MPa，退火，4.00 mm | 146 | ℃ | ASTM D648 |
| 维卡软化温度Vicat Softening Temperature | 151 | ℃ | ASTM D1525 6 |
| 球压温度Ball Indentation Temperature | 125 | ℃ | IEC 60598-1 |
| 线性热膨胀系数线性热膨胀系数 | |||
| MD：-40~82℃MD：-40 到 82℃ | 6.8E-5 | 1/℃ | ASTM D696 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 体积电阻率体积电阻率 | |||
| 23℃23℃ | 2.0E+17 | ohms·cm | ASTM D257 |
| 介电强度Electric Strength | 17 | kV/mm | ASTM D149 |
| 介电常数介电常数 | |||
| 60 Hz60 Hz | 3.00 | ASTM D150 | |
| 耗散因数耗散因数 | |||
| 60 Hz60 Hz | 1.0E-3 | ASTM D150 | |
| 相比漏电起痕指数漏电起痕指数 | |||
| 2.00 mm2.00 mm | 250 | V | IEC 60112 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级Flame Rating | UL 94 | ||
| 3.00 mm3.0 mm | HB | UL 94 | |
| 0.50 mm0.50 mm | V-2 | UL 94 | |
| 1.60 mm1.6 mm | V-2 | UL 94 | |
| 1.70 mm1.7 mm | V-2 | UL 94 | |
| 灼热丝起燃温度灼热丝起燃温度7 | |||
| 2 mm2.0 mm7 | 850 | ℃ | IEC 60695-2-13 |
| 极限氧指数Oxygen Index | 26 | % | ASTM D2863 |
| 平均燃烧程度Average Extent of Burning | 3 | cm | ASTM D635 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 折射率Refractive Index | 1.586 | ASTM D542 | |
| 透光率Transmittance | 89.0 | % | ASTM D1003 |
| 雾度Haze | 0.70 to 1.5 | % | ASTM D1003 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量Tensile Modulus | 2410 | MPa | ASTM D638 |
| 拉伸强度拉伸强度2 | |||
| 断裂断裂 | 72.0 | MPa | ASTM D638 |
| 屈服，23℃屈服，23℃2 | 60.0 | MPa | ASTM D638 |
| 拉伸应变拉伸应变 | |||
| 断裂断裂 | 150 | % | ASTM D638 |
| 屈服屈服 | 6.0 | % | ASTM D638 |
| 弯曲模量Flexural Modulus | 2410 | MPa | ASTM D790 |
| 弯曲强度Flexural Strength | 96.0 | MPa | ASTM D790 |
| 耐磨耗性耐磨耗性3 | |||
| Change in HazeChange in Haze3 | 45 | % | ASTM D1004 |
| 洛氏硬度Rockwell Hardness | ASTM D785 | ||
| M 级M-Scale | 74 | ASTM D785 | |
| R 级R-Scale | 118 | ASTM D785 | |