| 牌号简介About |
|---|
| Lupoy PC 1302-10树脂专为挤出和注塑产品设计。它在耐热性、透明度和冲击强度方面表现出良好的物理性能平衡。 |
产品描述Product Description
厂家：韩国LG化学LG Polymers India Pvt. Ltd.
类别：PCPolycarbonate
用途：薄膜;镜头;片材;电器用具;
加工条件：挤出Extrusion
性能特点：耐高温; 防火阻燃等级V-2; 透光性好; 冲击性能好;Good Clarity,High impact resistance,High Heat Resistance,V-2
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.20 | g/cm3 | ASTM D792 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 300℃，1.20kg300℃/1.2 kg | 10 | g/10min | ASTM D1238 |
| 收缩率收缩率 | |||
| MDMD | 0.50 到 0.70 | % | ASTM D955 |
| 吸水率Water Absorption | ASTM D570 | ||
| 23℃，24hr23°C, 24 hr | 0.15 | % | |
| 平衡，23℃，50% RHEquilibrium, 73°F, 50% RH | 0.32 | % | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 悬臂梁缺口冲击强度悬壁梁缺口冲击强度2 | |||
| 23℃，3.2mm23℃，3.20 mm2 | 900 | J/m | ASTM D256 |
| 悬臂梁无缺口冲击强度悬臂梁无缺口冲击强度 | |||
| 23℃23℃ | 无断裂 | ASTM D256 | |
| 装有测量仪表的落镖冲击装有测量仪表的落镖冲击3 | |||
| 23℃，3.20 mm，Total Energy23℃，3.20 mm，Total Energy3 | 87.0 | J | ASTM D3763 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa，退火，4.0 mm66 psi, Annealed, 0,157 in | 144 | ℃ | |
| 1.8 MPa，未退火，4.0 mm264 psi, Unannealed, 0,157 in | 128 | ℃ | |
| 1.8 MPa，退火，4.0 mm264 psi, Annealed, 0,157 in | 141 | ℃ | |
| 维卡软化温度Vicat Softening Temperature | 149 | ℃ | ASTM D1525 4 |
| 球压温度Ball Indentation Temperature | 125 | ℃ | IEC 60598-1 |
| 线性热膨胀系数线性热膨胀系数 | |||
| MD：-40~82℃MD：-40 到 82℃ | 6.8E-5 | 1/℃ | ASTM D696 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 体积电阻率体积电阻率 | |||
| 23℃23℃ | 2.0E+17 | ohms·cm | ASTM D257 |
| 介电强度Electric Strength | 17 | kV/mm | ASTM D149 |
| 介电常数介电常数 | |||
| 60 Hz60 Hz | 3.00 | ASTM D150 | |
| 耗散因数耗散因数 | |||
| 60 Hz60 Hz | 1.0E-3 | ASTM D150 | |
| 相比漏电起痕指数漏电起痕指数 | |||
| 2.00 mm2.00 mm | 250 | V | IEC 60112 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级Flame Rating | UL 94 | ||
| 0.50 mm0.500 mm | V-2 | ||
| 1.60 mm1.60 mm | V-2 | ||
| 2.50 mm2.50 mm | V-2 | ||
| 3.00 mm3.00 mm | V-2 | ||
| 灼热丝起燃温度灼热丝起燃温度5 | |||
| 2 mm2.00 mm5 | 850 | ℃ | IEC 60695-2-13 |
| 极限氧指数Oxygen Index | 26 | % | ASTM D2863 |
| 平均燃烧程度Average Extent of Burning | 3 | cm | ASTM D635 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 折射率Refractive Index | 1.586 | ASTM D542 | |
| 透光率Transmittance | 89.0 | % | ASTM D1003 |
| 雾度Haze | 0.70 到 1.5 | % | ASTM D1003 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 洛氏硬度Rockwell Hardness | ASTM D785 | ||
| M 级M 级 | 73 | ||
| R 级R 级 | 118 | ||
| 拉伸模量Tensile Modulus | 2410 | MPa | ASTM D638 |
| 拉伸强度Tensile Strength | ASTM D638 | ||
| 屈服Yield | 60.0 | MPa | |
| 断裂Break | 71.0 | MPa | |
| 拉伸应变Tensile Elongation | ASTM D638 | ||
| 屈服Yield | 6.0 | % | |
| 断裂Break | 150 | % | |
| 弯曲模量Flexural Modulus | 2410 | MPa | ASTM D790 |
| 弯曲强度Flexural Strength | 96.0 | MPa | ASTM D790 |
| 耐磨耗性耐磨耗性1 | |||
| Change in HazeChange in Haze1 | 45 | % | ASTM D1004 |