PC/ABS LUPOY ER5001RFA

Lupoy? ER5001RFA是一种聚碳酸酯 丙烯腈丁二烯苯乙烯(PC ABS)材料,含有的填充物为20% 玻璃纤维增强材料。 该产品在北美洲、拉丁美洲、欧洲或亚太地区有供货,加工方式为:注射成型。

Lupoy? ER5001RFA的主要特性有:

• 阻燃/额定火焰

• Flame Retardant

• 无卤素

Lupoy? ER5001RFA的典型应用领域为:电气/电子应用

PC/ABS LUPOY ER5001RFA

Physical Properties	Metric	English	Comments
Specific Gravity	1.18g/cc	1.18g/cc	ASTM D792
Maximum Moisture Content	0.020	0.020	Injection Molding
Linear Mold Shrinkage, Flow	0.0040-0.0060cm/cm @Thickness 3.20 mm	0.0040-0.0060in/in @Thickness 0.126 in	ASTM D955
Melt Flow	25g/10 min @Load 2.16 kg, Temperature 260 ?°C	25g/10 min @Load 4.76 lb, Temperature 500 ?°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	60.8MPa @Thickness 3.20 mm	8820psi @Thickness 0.126 in	50mm/min; ASTM D638
Flexural Yield Strength	97.1MPa @Thickness 3.20 mm	14100psi @Thickness 0.126 in	10mm/min; ASTM D790
Flexural Modulus	2.55GPa @Thickness 3.20 mm	370ksi @Thickness 0.126 in	10mm/min; ASTM D790
Izod Impact, Notched	=4.90J/cm @Thickness 3.20 mm, Temperature 23.0 ?°C	=9.18ft-lb/in @Thickness 0.126 in, Temperature 73.4 ?°F	ASTM D256

PC/ABS LUPOY ER5001RFA

简介

ABS工程塑料即PC ABS（工程塑料合金），在化工业的中文名字叫塑料合金，之所以命名为PC ABS，是因为这种材料既具有PC树脂的优良耐热耐候性、尺寸稳定性和耐冲击性能，又具有ABS树脂优良的加工流动性。所以应用在薄壁及复杂形状制品，能保持其优异的性能，以及保持塑料与一种酯组成的材料的成型性。ABS工程塑料最大的缺点就是质量重、导热性能欠佳。它的成型温度取于它们两者原料的之间温度，就是240-265度，温度太高ABS会分解，太低PC料的流动性不良。

PC/ABS应用

1.汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件

2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器

3.电信，移动电话外壳，附件以及智能卡（SIM卡）：

4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道

5.家用电器，如洗衣机，吹风机，微波炉内外部件

PC/ABS注塑模工艺条件:

干燥处理：加工前的干燥处理是必须的。湿度应小于0.04%，建议干燥条件为90~110C，2~4小时。

熔化温度： 230~300C。

模具温度：50~100C。

注射压力：取决于塑件。

注射速度：尽可能地高。