| 牌号简介About |
|---|
| PAXOTHENE? NA112-27（LDPE）具有较低的熔融指数和良好的韧性，特别适用于厚度为0.020~0.100 mm的薄膜。上述胶卷适用于购物袋、冷冻袋、可重封袋和收缩包装的包装应用。NA112-27具有中等滑度，使薄膜具有良好的可开启性。由NA112-27制成的吹塑薄膜的高光泽和低雾度特性为包装货物提供了诱人的外观，因此更有价值。 PAXOTHENE NA112-27 (LDPE) possesses low melt index and good toughness especially suitable for films with thickness of 0.020~0.100 mm. The said films are for package of shopping bags, frozen bags, re-closable bags and shrink packaging applications. NA112-27 is formulated with medium slip to give good openability of film. High gloss and low haze characteristics of blown film made from NA112-27 provide attractive appearance to the packaged goods thus more valuable. |
产品描述Product Description
厂家：台湾台聚USI Corporation
类别：LDPELDPE
用途：非特定食品应用;包装;袋子;食品包装;
加工条件：注射成型Injection Molding
性能特点：食品接触; 表面光泽度好; 韧性好;Good flexibility,Good surface appearance,Food contact compliance
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Density | 0.919 | g/cm3 | ASTM D1505 |
| 熔体质量流动速率Melt Mass-Flow Rate (MFR) | 3.0 | g/10min | ASTM D1238 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 邵氏硬度邵氏硬度 | |||
| 邵氏 D邵氏 D | 52 | ASTM D2240 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸强度Tensile Strength | ASTM D882 | ||
| MD，屈服MD : Yield | 8.92 | MPa | ASTM D882 |
| TD，屈服TD : Yield | 8.92 | MPa | ASTM D882 |
| MD，断裂MD : Break | 18.6 | MPa | ASTM D882 |
| TD，断裂TD : Break | 15.1 | MPa | ASTM D882 |
| 拉伸应变Tensile Elongation | ASTM D882 | ||
| MD，断裂MD : Break | 340 | % | ASTM D882 |
| TD，断裂TD : Break | 550 | % | ASTM D882 |
| 落锤冲击Gardner Impact 22 | 110 | g | ASTM D1709 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 脆化温度Brittleness Temperature | -76.0 | ℃ | ASTM D746 |
| 维卡软化温度Vicat Softening Temperature | 100 | ℃ | ASTM D1525 |
| 熔融峰值温度Peak Melting Temperature | 108 | ℃ | ASTM D3418 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 光泽度Gardner光泽度 | |||
| 60°60° | 100 | ASTM D523 | |
| 雾度Haze | 7.0 | % | ASTM D1003 |