LDPE台湾台聚NA205-15 低密度聚乙烯可热封食品级PE原材料|价格|厂家|多少钱-全球塑胶网-移动端

牌号简介About
PAXOTHENE? NA205-15（LDPE）是专为纸张、玻璃纸、铝箔、聚烯烃膜、聚酯膜、尼龙膜等各种基材挤出涂布而研制的。NA205-15对纸张等各种多孔基材以及玻璃纸和箔纸等非多孔基材也具有良好的粘附性。低透湿率和良好的热封性使NA205-15成为一种良好的涂层材料。在可加工性方面，NA205-15具有良好的流动特性和较低的缩颈，提供了较高的生产线速度，减少了挤出涂层中树脂的损失。 PAXOTHENE NA205-15 (LDPE) is specially developed for extrusion coating on various substrates such as paper, cellophane, aluminum foil, polyolefin film, polyester film and nylon film. NA205-15 also possesses excellent adhesion to a variety of porous substrates such as paper as well as non-porous substrates such as cellophane and foil. Low moisture-vapor transmission rates in combination with excellent heat sealability makes NA205-15 a good coating material. Concerning processability, good flow characteristics and low neck-in of NA205-15 provide high line speed and reduce the loss of resin in the extrusion coating.

牌号简介About

PAXOTHENE? NA205-15（LDPE）是专为纸张、玻璃纸、铝箔、聚烯烃膜、聚酯膜、尼龙膜等各种基材挤出涂布而研制的。NA205-15对纸张等各种多孔基材以及玻璃纸和箔纸等非多孔基材也具有良好的粘附性。低透湿率和良好的热封性使NA205-15成为一种良好的涂层材料。在可加工性方面，NA205-15具有良好的流动特性和较低的缩颈，提供了较高的生产线速度，减少了挤出涂层中树脂的损失。 PAXOTHENE NA205-15 (LDPE) is specially developed for extrusion coating on various substrates such as paper, cellophane, aluminum foil, polyolefin film, polyester film and nylon film. NA205-15 also possesses excellent adhesion to a variety of porous substrates such as paper as well as non-porous substrates such as cellophane and foil. Low moisture-vapor transmission rates in combination with excellent heat sealability makes NA205-15 a good coating material. Concerning processability, good flow characteristics and low neck-in of NA205-15 provide high line speed and reduce the loss of resin in the extrusion coating.

产品描述Product Description

厂家：台湾台聚USI Corporation

类别：LDPELDPE

用途：涂层应用;

加工条件：挤出涂层

性能特点：粘结性好; 内缩量低; 食品接触; 低密度; 易流动; 热封性好;Good heat sealing,Good liquidity,Low shrinkage,Food contact compliance,Good bond,Low density

技术参数Technical Data
物理性能	额定值Nominal Value	单位Units	测试方法Test Method
密度Density	0.919	g/cm3	ASTM D1505
熔体质量流动速率Melt Mass-Flow Rate (MFR)	3.0	g/10min	ASTM D1238
机械性能	额定值Nominal Value	单位Units	测试方法Test Method
邵氏硬度邵氏硬度
邵氏 D邵氏 D	53		ASTM D2240
薄膜	额定值Nominal Value	单位Units	测试方法Test Method
拉伸强度Tensile Strength			ASTM D882
MD，屈服MD : Yield	9.02	MPa	ASTM D882
TD，屈服TD : Yield	9.02	MPa	ASTM D882
MD，断裂MD : Break	19.1	MPa	ASTM D882
TD，断裂TD : Break	15.4	MPa	ASTM D882
拉伸应变Tensile Elongation			ASTM D882
MD，断裂MD : Break	330	%	ASTM D882
TD，断裂TD : Break	540	%	ASTM D882
落锤冲击Gardner Impact	98	g	ASTM D1709
热性能	额定值Nominal Value	单位Units	测试方法Test Method
脆化温度Brittleness Temperature	-76.0	℃	ASTM D746
维卡软化温度Vicat Softening Temperature	100	℃	ASTM D1525
熔融峰值温度Peak Melting Temperature	109	℃	ASTM D3418
光学性能	额定值Nominal Value	单位Units	测试方法Test Method
光泽度Gardner光泽度
60°60°	100		ASTM D523
雾度Haze	6.0	%	ASTM D1003