ATTANE? 4404G
ULDPE
陶氏化学(Dow Chemical)
产品描述
Provides improved cling in one-sided cling applications
It has improved toughness and optical properties
Complies with:
Canadian HPFB No Objection (with limitations)
EU, No 10/2011
U.S. FDA CFR 176.170(c)
U.S. FDA FCN 424
Consult the regulations for complete details.
基本信息
| 原厂资料 | 物性表-ASTM(英文) |
|||
| 法规认证 | EU Food Contact(2011/10/EC)(欧盟食品级)FDA(食品药品监督管理局)HPFB (加拿大健康产品和食品局) |
|||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 |
0.904 g/cm3 | ASTM D792 | |
密度 |
0.904 g/cm3 | Internal | Base Density |
熔体质量流动速率(MFR) |
|||
190℃/2.16 kg |
4 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) |
71.1 °C | ASTM D1525 | |
熔融温度(Tm) |
124 °C | Internal | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透明度 |
99 - | ASTM D1746 | 20.3 μm |
透明度 |
99 - | ASTM D1746 | 50.8 μm |
雾度 |
0.6 % | ASTM D1003 | 20.3 μm |
雾度 |
1.8 % | ASTM D1003 | 50.8 μm |
光泽度 |
92 - | ASTM D 2457 | 45°, 20.3 μm |
光泽度 |
90 - | ASTM D 2457 | 45°, 50.8 μm |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 |
|||
屈服(yld) |
7 Mpa | ASTM D 882 | MD, 20 μm |
屈服(yld) |
6.76 Mpa | ASTM D 882 | MD, 51μm |
屈服(yld) |
4.92 Mpa | ASTM D 882 | TD, 20 μm |
屈服(yld) |
6.34 Mpa | ASTM D 882 | TD, 51 μm |
断裂(brk) |
36.9 Mpa | ASTM D 882 | MD, 20 μm |
断裂(brk) |
32.6 Mpa | ASTM D 882 | MD, 51μm |
断裂(brk) |
29.1 Mpa | ASTM D 882 | TD, 20 μm |
断裂(brk) |
32.4 Mpa | ASTM D 882 | TD, 51 μm |
拉伸延伸率 |
|||
断裂(brk) |
500 % | ASTM D 882 | MD, 20 μm |
断裂(brk) |
660 % | ASTM D 882 | MD, 51μm |
断裂(brk) |
710 % | ASTM D 882 | TD, 20 μm |
断裂(brk) |
710 % | ASTM D 882 | TD, 51 μm |
耐穿透性 |
18.9 J/cm3 | Internal | 20 μm |
耐穿透性 |
17.5 J/cm3 | Internal | 51 μm |
埃尔曼多夫撕裂 |
330 g | ASTM D 1922 | MD, 20 μm |
埃尔曼多夫撕裂 |
960 g | ASTM D 1922 | MD, 51μm |
埃尔曼多夫撕裂 |
500 g | ASTM D 1922 | TD, 20 μm |
埃尔曼多夫撕裂 |
1100 g | ASTM D 1922 | TD, 51 μm |
割线模量 |
58.8 Mpa | ASTM D 882 | 2% Secant, MD, 20 μm |
割线模量 |
62.6 Mpa | ASTM D 882 | 2% Secant, MD, 51 μm |
割线模量 |
64.7 Mpa | ASTM D 882 | 2% Secant, TD, 20 μm |
割线模量 |
63 Mpa | ASTM D 882 | 2% Secant, TD, 51 μm |
落锤冲击 |
850 g | ASTM D 1709 | 20 μm |
落锤冲击 |
850 g | ASTM D 1709 | 51 μm |
水蒸气渗透系数 |
0.85 g.mm/m2.24hr | ASTM F 1249 | 51 μm |
氧渗透 |
450 cm3·mm/m2/atm/24 hr | ASTM D 3985 | 23°C, 51 μm |
二氧化碳渗透 |
2000 cm3·mm/m2/atm/24 hr | Internal | 23°C, 50.8 μm |
特性：
1、外观似低密度聚乙烯，分子结构接近高密度聚乙烯。
2、刚性类似高密度聚乙烯，抗撕裂强度、拉伸强度、耐冲击和低温冲击性、耐穿刺性、耐环境压力开裂性和耐蠕变性优于低密度聚乙烯。
3、熔点为120-125C
4、耐低温性能优于LDPE和HDPE。
产业应用及其产品：
1、70%的产品用于吹塑薄膜、共挤出薄膜、复活薄膜和收缩薄膜。
2、重包装袋、食品轻纺工业包装袋，杂品包装袋、大容积包装袋、农业薄膜等。
3、管材和电线电缆包覆。
4、气密性容器的盖、内塞、化学品容器、农药的容器槽车罐和贮槽等大型容器。
5、汽车零件。
6、若 LDPE/LLDPE混合料（60：40--70：30）制得薄膜，厚度可减少30-40%。
ULDPE超低密度聚乙烯
超低密度聚乙烯为半透明颗粒。透明度高,无毒、无味、无臭。密度为0.905~0.915g/cm3。性质较柔软，具有良好的延伸性、电绝缘性、化学稳定性、加工性能和耐低温
石油工业上所称低密度聚乙烯(即高压聚乙烯)是一种塑料材料，他适合热塑性成型加工的各种成型工艺．成型加工性好， 如注塑、挤塑、吹塑、旋转成型、涂覆、发泡工艺、热成型、热风焊、热焊接等。