| 说明：鲁特尼FB3000主要用于挤出机械性能高的吹塑薄膜，用于所有厚度的透明袋。叶黄素FB3000具有很高的机械性能，能够生产非常薄、透明、有光泽的薄膜。（鲁特尼FB3000含有滑动剂和防堵剂。）主要用途：各种厚度的透明袋、自动包装用薄膜、纺织品包装、轻型运输袋、包装用收缩膜、层压膜。 Description LUTENE FB3000 is mainly intended for the extrusion of blown film with high mechanical property for the clarity bags in all thickness. LUTENE FB3000 have high mechanical property and enables the production of very thin, clear, glossy film. (LUTENE FB3000 contains slip agent and antiblock agent.) Main Applications Clarity bags in all thicknesses, film for automatic packaging, packing of textiles, lightweight carrier bags, shrink film for packing, film for lamination |
产品描述Product Description
厂家：韩国LG化学LG Polymers India Pvt. Ltd.
类别：PEPE
用途：薄膜;包装;袋子;层压板;吹膜;
加工条件：吹塑薄膜
性能特点：抗结块性; 高光滑性;Smoothness,High anti-blocking
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度密度22 | 0.921 | g/cm3 | ASTM D1505 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 190℃，2.16kg190℃/2.16 kg | 3.0 | g/10min | ASTM D1238 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 摩擦系数Coefficient of Friction | 0.080 | ASTM D1894 | |
| 撕裂阻力Tear Resistance | |||
| MD：50.0 μmMD : 50.0 μm | 88.3 | kN/m | |
| TD：50.0 μmTD : 50.0 μm | 83.4 | kN/m | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 薄膜厚度薄膜厚度 | |||
| 测试经测试 | 50 | μm | |
| 拉伸强度Tensile Strength | |||
| MD，断裂，50 μmMD : Break, 2.0 mil | 18.6 | MPa | |
| TD，断裂，50 μmTD : Break, 2.0 mil | 18.1 | MPa | |
| 拉伸应变Tensile Elongation | |||
| MD，断裂，50 μmMD : Break, 2.0 mil | 420 | % | |
| TD，断裂，50 μmTD : Break, 2.0 mil | 610 | % | |
| 落锤冲击落锤冲击 | |||
| 50 μm50 μm | 110 | g | ASTM D1709 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 维卡软化温度Vicat Softening Temperature | 90.0 | ℃ | ASTM D1525 |
| 熔融温度Melting Temperature | 110 | ℃ | DSC |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 光泽度光泽度 | |||
| 60°，50.0 μm60°，50.0 μm | 95 | ASTM D2457 | |
| 雾度雾度 | |||
| 50 μm50.0 μm | 8.0 | % | ASTM D1003 |