| 牌号简介About |
|---|
| LG PMMA IH830是一种聚甲基丙烯酸甲酯-丙烯酸材料,。 该产品在亚太地区、北美洲、拉丁美洲或欧洲有供货,加工方式为:注射成型。 LG PMMA IH830的主要特性有: 阻燃/额定火焰 通过 ROHS 认证 LG PMMA IH830的典型应用领域为:汽车行业 LG PMMA IH830 is a Polymethyl Methacrylate Acrylic material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of LG PMMA IH830 are: Flame Rated RoHS Compliant Typical application of LG PMMA IH830: Automotive |
产品描述Product Description
厂家：韩国LG MMA
类别：PMMAPMMA
用途：通用;
加工条件：注射成型Injection Molding
性能特点：防火阻燃等级HB;HB
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.18 | g/cm3 | ASTM D792 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 230℃，3.80kg230℃/3.8 kg | 2.3 | g/10min | ASTM D1238 |
| 收缩率收缩率 | |||
| MDMD | 0.20 to 0.60 | % | ASTM D955 |
| 吸水率吸水率 | |||
| 24hr24 hr | 0.30 | % | ASTM D570 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | 1.4 | kJ/m2 | ISO 179-1eA |
| 简支梁无缺口冲击强度Charpy Unnotched Impact Strength | 15 | kJ/m2 | ISO 179/1eU |
| 悬臂梁缺口冲击强度悬壁梁缺口冲击强度 | |||
| AreaArea | 1.50 | kJ/m2 | ASTM D256 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火1.8 MPa，未退火 | 101 | ℃ | ASTM D648 |
| 维卡软化温度Vicat Softening Temperature | 114 | ℃ | ASTM D1525 2 |
| 线性热膨胀系数线性热膨胀系数 | |||
| MDMD | 6.0E-5 | 1/℃ | ASTM D696 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 体积电阻率Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| 介电强度Dielectric Strength 33 | 20 | kV/mm | ASTM D149 |
| 介电常数介电常数 | |||
| 60 Hz60 Hz | 3.10 | ASTM D150 | |
| 耗散因数耗散因数 | |||
| 60 Hz60 Hz | 0.050 | ASTM D150 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级Flame Rating | HB | UL 94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 折射率Refractive Index | 1.490 | ASTM D542 | |
| 透光率透射率 | |||
| 3200 μm3200 μm | 92.0 | % | ASTM D1003 |
| 雾度雾度 | |||
| 3200 μm3200 μm | 0.10 | % | ASTM D1003 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸强度拉伸强度 | |||
| 屈服屈服 | 70.6 | MPa | ASTM D638 |
| 拉伸应变拉伸应变 | |||
| 屈服屈服 | 13 | % | ASTM D638 |
| 弯曲模量Flexural Modulus | 3410 | MPa | ASTM D790 |
| 弯曲强度弯曲强度 | |||
| 屈服屈服 | 135 | MPa | ASTM D790 |
| 洛氏硬度洛氏硬度 | |||
| M 级M 级 | 98 | ASTM D785 | |