江苏普及塑料有限公司
| 牌号简介About |
|---|
| Cycoloy C6600聚碳酸酯/丙烯腈-丁二烯-苯乙烯（PC/ABS）树脂是一种可注射成型的标准级树脂。这种无氯化、无溴阻燃PC/ABS具有UL V0和5VB的阻燃等级。Cycoloy C6600树脂是多种应用的理想选择，包括商用设备、显示器和外壳。 CYCOLOY C6600 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a standard grade that can be injection molded. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 5VB flame rating. CYCOLOY C6600 resin is an excellent candidate for a wide variety of applications including business equipment, monitors, and enclosures. |
产品描述Product Description
厂家：沙特沙伯基础SABIC
类别：PC+ABSPC+ABS
用途：室外应用;医疗/护理用品;非特定食品应用;电子显示器;Automotive Lighting;商业设备;汽车外部零件;监测器;密封罩;薄壁包装;
加工条件：注射成型Injection Molding
性能特点：无卤; 防火阻燃等级V-0; 防火阻燃等级V-2; 防火阻燃等级5VB; 耐水解; 阻燃; 冲击性能好; 易流动;High impact resistance,Hydrolysis stability,Good liquidity,Halogen free,Flame Characteristics,V-2,V-0,5VB
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.19 | g/cm3 | ASTM D792 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 260℃，2.16kg260℃/2.16 kg | 22 | g/10min | ASTM D1238 |
| 收缩率收缩率 | |||
| MD：3.2 mmMD，3.20 mm | 0.40 to 0.60 | % | 内部方法 |
| 吸水率吸水率 | |||
| 24hr24 hr | 0.11 | % | ASTM D570 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量Tensile Modulus 22 | 3000 | MPa | ASTM D638 |
| 拉伸强度拉伸强度3 | |||
| 断裂断裂3 | 49.0 | MPa | ASTM D638 |
| 屈服屈服3 | 63.0 | MPa | ASTM D638 |
| 拉伸应变拉伸应变3 | |||
| 断裂断裂4 | 80 | % | ASTM D638 |
| 屈服屈服3 | 4.0 | % | ASTM D638 |
| 弯曲模量弯曲模量4 | |||
| 50 mm跨距50.0 mm 跨距4 | 2620 | MPa | ASTM D790 |
| 弯曲强度弯曲强度4 | |||
| 屈服，50 mm跨度屈服，50.0 mm 跨距4 | 94.0 | MPa | ASTM D790 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 悬臂梁缺口冲击强度悬壁梁缺口冲击强度 | |||
| 23℃23℃ | 550 | J/m | ASTM D256 |
| 装有测量仪表的落镖冲击Instrumented Dart Impact | ASTM D3763 | ||
| -30℃，总能量-30°C，总能量 | 51.0 | J | ASTM D3763 |
| 23℃，总能量23°C，总能量 | 51.0 | J | ASTM D3763 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa，未退火，6.4 mm0.45 MPa，未退火，6.40 mm | 98.0 | ℃ | ASTM D648 |
| 1.8 MPa，未退火，3.2 mm264 psi, Unannealed, 0.126 in | 83.0 | ℃ | ASTM D648 |
| 1.8 MPa，未退火，6.4 mm264 psi, Unannealed, 0.252 in | 90.0 | ℃ | ASTM D648 |
| 维卡软化温度Vicat Softening Temperature | 99.0 | ℃ | ASTM D1525 5 |
| 相对温度指数相对温度指数 | |||
| 静态静态 | 80.0 | ℃ | UL 746 |
| 电气性能电气特性 | 80.0 | ℃ | UL 746 |
| 冲击机械性能机械冲击性能 | 70.0 | ℃ | UL 746 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 表面电阻率Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| 体积电阻率Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| 介电强度介电强度 | |||
| 3.2 mm，在油中3.20 mm，在油中 | 17 | kV/mm | IEC 60243-1 |
| 相对电容率Relative Permittivity | IEC 60250 | ||
| 50 Hz50 Hz | 2.70 | IEC 60250 | |
| 60 Hz60 Hz | 2.70 | IEC 60250 | |
| 1 MHz1 MHz | 2.70 | IEC 60250 | |
| 耗散因数Dissipation Factor | IEC 60250 | ||
| 50 Hz50 Hz | 4.0E-3 | IEC 60250 | |
| 60 Hz60 Hz | 4.0E-3 | IEC 60250 | |
| 1 MHz1 MHz | 6.0E-3 | IEC 60250 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级Flame Rating | UL 94 | ||
| 0.75 mm0.75 mm | V-2 | UL 94 | |
| 1.50 mm1.5 mm | V-0 | UL 94 | |
| 2.00 mm2.0 mm | 5VB | UL 94 | |