江苏普及塑料有限公司
| 牌号简介About |
|---|
| PA 6-共聚物，15%玻璃纤维，注塑成型，提高冲击强度，热老化稳定 Durethan? BKV215H2.0 900051 DUS035 (Dry) PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized Durethan? BKV215H2.0 900051 DUS035 PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized Durethan? BKV215H2.0 900051 DUS035 PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized |
产品描述Product Description
厂家：德国朗盛LANXESS Asia/Pacific
类别：PA6PA6
加工条件：注射成型Injection Molding
性能特点：热稳定性好; 共聚物; 冲击性能好;High impact resistance,Copolymer,Heat Stabilized
填料：玻璃纤维 15
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度密度(23°C) | 1.17 | g/cm3 | |
| 表观密度Apparent Density | 0.60 | g/cm3 | |
| 收缩率Molding Shrinkage | |||
| TD：120℃，2.0 mm横向流量 : 120°C, 2.00 mm22 | 0.10 | % | |
| TD：280℃，2.0 mm横向流量 : 280°C, 2.00 mm33 | 0.80 | % | |
| MD：120℃，2.0 mm流量 : 120°C, 2.00 mm22 | 0.10 | % | |
| MD：280℃，2.0 mm流量 : 280°C, 2.00 mm33 | 0.50 | % | |
| 吸水率Water Absorption | |||
| 饱和，23℃Saturation, 73°F | 7.0 | % | |
| 平衡，23℃，50% RHEquilibrium, 73°F, 50% RH | 2.0 | % | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | |||
| -30℃-30°C | 10 | kJ/m2 | |
| 简支梁无缺口冲击强度Charpy Unnotched Impact Strength | |||
| -30℃-30°C | 80 | kJ/m2 | |
| 23℃23°C | 70 | kJ/m2 | |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | |||
| 23℃23°C | 20 | kJ/m2 | |
| 悬臂梁无缺口冲击强度Unnotched Izod Impact Strength | |||
| -30℃-30°C | 65 | kJ/m2 | |
| 23℃23°C | 60 | kJ/m2 | |
| 多轴向仪器化冲击能量Multi-Axial Instrumented Impact Energy | |||
| -30℃，冲击总贯穿能量-30°C, 冲击总贯穿能量 | 4.00 | J | |
| 23℃，冲击总贯穿能量23°C, 冲击总贯穿能量 | 10.0 | J | |
| 多轴向仪器化冲击力峰值Multi-Axial Instrumented Impact Peak Force | |||
| -30℃-30°C | 750 | N | |
| 23℃23°C | 1500 | N | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Heat Deflection Temperature | |||
| 0.45 MPa，未退火66 psi, Unannealed | 200 | ℃ | |
| 1.8 MPa，未退火264 psi, Unannealed | 175 | ℃ | |
| 维卡软化温度Vicat Softening Temperature | 200 | ℃ | |
| 熔融温度熔融温度66 | 214 | ℃ | |
| 线性热膨胀系数CLTE | |||
| MD：23~55℃Flow : 73 to 131°F | 4.0E-5 | 1/℃ | |
| TD：23~55℃Transverse : 73 to 131°F | 1.5E-4 | 1/℃ | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| ISO ShortnameISO Shortname | ISO 1874-PA 6/66-HI, GHR, 14-040, GF15 | ||
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 球压硬度Ball Indentation Hardness | 120 | MPa | |
| 拉伸模量拉伸模量 | |||
| 23℃23℃ | 4300 | MPa | |
| 拉伸强度拉伸强度 | |||
| 断裂，23℃断裂，23℃ | 85.0 | MPa | |
| 拉伸应变拉伸应变 | |||
| 断裂，23℃断裂，23℃ | 4.5 | % | |
| 弯曲模量弯曲模量4 | |||
| 23℃23℃4 | 4000 | MPa | |
| 弯曲强度弯曲应力44 | |||
| 23℃23°C | 135 | MPa | |
| 3.50% 应变，23℃3.5% 应变, 23°C | 120 | MPa | |
| 弯曲应变Flexural Strain at Flexural Strength5(23°C)5 | 5.5 | % | |