江苏普及塑料有限公司
| 牌号简介About |
|---|
| Ultramid? 8202C HS是一种热稳定、低粘度、PA6注塑成型均聚物，具有改进的结晶结构，以提高性能和更快的周期。它也有彩色版本。应用Ultramid? 8202C HS通常推荐用于齿轮、阀门、配件、绝缘体、衬套、滑块、窗五金、布线装置、纺织部件和家具脚轮等应用。 Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also available in pigmented versions. Applications Ultramid 8202C HS is generally recommended for applications such as gears, valves, fittings, insulators, bushings, slides, window hardware, wiring devices, textile components and furniture casters. |
产品描述Product Description
厂家：德国巴斯夫BASF Polyurethanes GmbH
类别：PA6PA6
用途：阀门/阀门部件;电气元件;衬套;纺织应用;家具;齿轮;绝缘材料;配件;
颜色：可用颜色
加工条件：注射成型Injection Molding
性能特点：热稳定性好; 成型周期快; 均聚物; 防火阻燃等级V-2; 低粘度; 结晶;Low Viscosity,Crystal,Quick molding cycle,Heat Stabilized,Homopolymer,V-2
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.13 | g/cm3 | ASTM D792 |
| 密度Density | 1.13 | g/cm3 | ISO 1183 |
| 收缩率收缩率 | |||
| MD：3.2 mmMD，3.18 mm | 0.90 | % | |
| 吸水率吸水率 | |||
| 饱和，23℃饱和，23℃ | 9.3 | % | ISO 62 |
| 饱和饱和 | 9.3 | % | ASTM D570 |
| 平衡，23℃，50% RH平衡，23℃，50% RH | 2.6 | % | ISO 62 |
| 平衡，50% RHEquilibrium，50% RH | 2.6 | % | ASTM D570 |
| 24hr24 hr | 1.6 | % | ASTM D570 |
| 23℃，24hr23℃，24 hr | 1.6 | % | ISO 62 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度简支梁缺口冲击强度 | |||
| 23℃23℃ | 3.5 | kJ/m2 | ISO 179 |
| 简支梁无缺口冲击强度简支梁无缺口冲击强度 | |||
| 23℃23℃ | No Break | ISO 179 | |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | ASTM D256 | ||
| -40℃-40°C | 32 | J/m | ASTM D256 |
| 23℃23°C | 48 | J/m | ASTM D256 |
| 落下冲击阻力落下冲击阻力 | |||
| 23℃23℃ | 122 | J | Internal Method |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火1.8 MPa，未退火 | 65.0 | ℃ | ISO 75-2/A |
| 1.8 MPa，未退火1.8 MPa，未退火 | 75.0 | ℃ | ASTM D648 |
| 0.45 MPa，未退火0.45 MPa，未退火 | 190 | ℃ | ASTM D648 |
| 0.45 MPa，未退火0.45 MPa，未退火 | 165 | ℃ | ISO 75-2/B |
| 熔融峰值温度Peak Melting Temperature | 220 | ℃ | ASTM D3418 |
| 熔融温度溶融温度 | |||
| DSCDSC | 220 | ℃ | ISO 3146 |
| 线性热膨胀系数线性热膨胀系数 | |||
| MDMD | 8.1E-5 | 1/℃ | ASTM E831 |
| 相对温度指数相对温度指数 | |||
| 电气性能电气性能 | UL 746 | ||
| 0.71 mm0.71 mm | 130 | ℃ | UL 746 |
| 1.5 mm1.5 mm | 130 | ℃ | UL 746 |
| 3.0 mm3.0 mm | 130 | ℃ | UL 746 |
| 6.0 mm6.0 mm | 130 | ℃ | UL 746 |
| 强度机械性能强度机械性能 | UL 746 | ||
| 0.71 mm0.71 mm | 95.0 | ℃ | UL 746 |
| 3.0 mm3.0 mm | 105 | ℃ | UL 746 |
| 冲击机械性能冲击机械性能 | UL 746 | ||
| 1.5 mm1.5 mm | 105 | ℃ | UL 746 |
| 6.0 mm6.0 mm | 105 | ℃ | UL 746 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 体积电阻率Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| 1.50 mm1.50 mm | 1.0E+13 | ohms·cm | ASTM D257 |
| 介电强度介电强度2 | |||
| 1.5 mm1.50 mm2 | 30 | kV/mm | ASTM D149 |
| 相比漏电起痕指数Comparative Tracking Index | 600 | V | IEC 60112 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级Flame Rating | UL 94 | ||
| 0.71 mm0.71 mm | V-2 | UL 94 | |
| 1.50 mm1.5 mm | V-2 | UL 94 | |
| 3.00 mm3.0 mm | V-2 | UL 94 | |
| 6.00 mm6.0 mm | V-2 | UL 94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量Tensile Modulus | ISO 527-2 | ||
| -40℃-40°C | 4090 | MPa | ISO 527-2 |
| 23℃23°C | 3700 | MPa | ISO 527-2 |
| 80℃80°C | 750 | MPa | ISO 527-2 |
| 120℃120°C | 550 | MPa | ISO 527-2 |
| 150℃150°C | 445 | MPa | ISO 527-2 |
| 拉伸强度Tensile Stress | ISO 527-2 | ||
| 屈服，-40℃Yield, -40°F | 137 | MPa | ISO 527-2 |
| 屈服，23℃Yield, 73°F | 88.0 | MPa | ISO 527-2 |
| 屈服，80℃Yield, 176°F | 40.0 | MPa | ISO 527-2 |
| 屈服，120℃Yield, 248°F | 30.0 | MPa | ISO 527-2 |
| 屈服，150℃Yield, 302°F | 25.0 | MPa | ISO 527-2 |
| 拉伸强度Tensile Strength | ASTM D638 | ||
| 断裂，-40℃Break, -40°F | 130 | MPa | ASTM D638 |
| 断裂，23℃Break, 73°F | 90.0 | MPa | ASTM D638 |
| 断裂，80℃Break, 176°F | 35.0 | MPa | ASTM D638 |
| 断裂，121℃Break, 121°C | 25.0 | MPa | ASTM D638 |
| 拉伸应变Tensile Elongation | ASTM D638 | ||
| 屈服，23℃屈服，23℃ | 4.0 | % | ISO 527-2 |
| 断裂，-40℃Break, -40°F | 5.0 | % | ASTM D638 |
| 断裂，23℃Break, 73°F | 12 | % | ASTM D638 |
| 断裂，80℃Break, 176°F | 100 | % | ASTM D638 |
| 断裂，121℃Break, 121°C | 100 | % | ASTM D638 |
| 标称拉伸断裂应变Nominal Tensile Strain at Break | ISO 527-2 | ||
| -40℃-40°C | 5.0 | % | ISO 527-2 |
| 23℃23°C | 7.0 | % | ISO 527-2 |
| 80℃80°C | 100 | % | ISO 527-2 |
| 120℃120°C | 100 | % | ISO 527-2 |
| 弯曲模量Flexural Modulus | ASTM D790 | ||
| 23℃23℃ | 2800 | MPa | ISO 178 |
| -40℃-40°C | 3370 | MPa | ASTM D790 |
| 23℃23°C | 3170 | MPa | ASTM D790 |
| 65℃65°C | 600 | MPa | ASTM D790 |
| 90℃90°C | 440 | MPa | ASTM D790 |
| 121℃121°C | 385 | MPa | ASTM D790 |
| 弯曲强度Flexural Strength | ASTM D790 | ||
| 23℃23℃ | 95.0 | MPa | ISO 178 |
| -40℃-40°C | 183 | MPa | ASTM D790 |
| 23℃23°C | 110 | MPa | ASTM D790 |
| 65℃65°C | 30.0 | MPa | ASTM D790 |
| 121℃121°C | 21.0 | MPa | ASTM D790 |
| 洛氏硬度洛氏硬度 | |||
| R 级R 级 | 120 | ASTM D785 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 屈服，-40℃Yield, -40°F | 137 | MPa | ASTM D638 |
| 屈服，23℃Yield, 73°F | 90.0 | MPa | ASTM D638 |
| 屈服，80℃Yield, 176°F | 40.0 | MPa | ASTM D638 |
| 屈服，121℃Yield, 121°C | 30.0 | MPa | ASTM D638 |
| 屈服，-40℃Yield, -40°F | 3.0 | % | ASTM D638 |
| 屈服，23℃Yield, 73°F | 4.0 | % | ASTM D638 |
| 屈服，80℃Yield, 176°F | 25 | % | ASTM D638 |
| 屈服，121℃Yield, 121°C | 27 | % | ASTM D638 |