PA6德国巴斯fu/B3GM35耐油性能矿纤增强注塑挤出级|价格|厂家|多少钱-全球塑胶网-移动端

牌号简介About
Ultramid? B3GM35 BK60564是一种40%组合玻璃纤维和矿物增强，色素黑色注塑成型PA6级。典型应用包括要求中等硬度和高尺寸稳定性的工业产品。 Ultramid B3GM35 BK60564 is a 40% combined glass-fiber and mineral reinforced, pigmented black injection molding PA6 grade. Applications Typical applications include industrial articles requiring medium rigidity and high dimensional stability.

牌号简介About

Ultramid? B3GM35 BK60564是一种40%组合玻璃纤维和矿物增强，色素黑色注塑成型PA6级。典型应用包括要求中等硬度和高尺寸稳定性的工业产品。 Ultramid B3GM35 BK60564 is a 40% combined glass-fiber and mineral reinforced, pigmented black injection molding PA6 grade. Applications Typical applications include industrial articles requiring medium rigidity and high dimensional stability.

产品描述Product Description

厂家：德国巴斯夫BASF Polyurethanes GmbH

类别：PA6PA6

用途：工业应用;

颜色：黑色

加工条件：注射成型Injection Molding

性能特点：尺寸稳定性好; 耐油;Good Dimensional Stability,Grease resistance

填料：玻璃纤维/矿物 40

技术参数Technical Data
物理性能	额定值Nominal Value	单位Units	测试方法Test Method
密度Density	1.48	g/cm3	ISO 1183
吸水率吸水率
饱和，23℃饱和，23℃	5.7	%	ISO 62
平衡，23℃，50% RH平衡，23℃，50% RH	1.7	%	ISO 62
机械性能	额定值Nominal Value	单位Units	测试方法Test Method
拉伸模量拉伸模量
23℃23℃	8300	MPa	ISO 527-2
拉伸强度拉伸强度
断裂，23℃断裂，23℃	128	MPa	ISO 527-2
拉伸应变拉伸应变
断裂，23℃断裂，23℃	3.0	%	ISO 527-2
弯曲模量弯曲模量
23℃23℃	7550	MPa	ISO 178
冲击性能	额定值Nominal Value	单位Units	测试方法Test Method
悬臂梁缺口冲击强度Notched Izod Impact Strength			ISO 180
-40℃-40°C	3.9	kJ/m2	ISO 180
23℃23°C	5.4	kJ/m2	ISO 180
热性能	额定值Nominal Value	单位Units	测试方法Test Method
熔融温度溶融温度
DSCDSC	220	℃	ISO 3146